Influence of gadolinium on solidification behavior of Ni–Mo-Cr-Gd alloy
Xin Fu,Qing-Chun Zhu,Li Jiang,Fang Liu,Zhi-Jun Li
DOI: https://doi.org/10.1016/j.jallcom.2023.169904
IF: 6.2
2023-04-05
Journal of Alloys and Compounds
Abstract:The influence of Gd content on the solidification behaviors and as-cast microstructures of Ni–Mo-Cr-Gd alloy have been investigated systematically. It was found that the γ/Ni 5 Gd eutectic phases were formed in the interdendritic region, which exhibits the divorced character. With the Gd adding, the γ/M 6 C eutectic phases were replaced by the γ/M 2 C eutectic ones. Most M 2 C carbides locate at the interfaces of γ/Ni 5 Gd eutectic phases or are enclosed by Ni 5 Gd phases. The segregation of alloying elements was mitigated by Gd adding. Based on the thermal analysis, composition analysis and thermodynamic calculation, the solidification behaviors, and the affecting mechanism of Gd adding were briefly discussed. During the solidification process, the γ/Ni 5 Gd eutectic reaction occurs first, which interrupts the solute redistribution process and thus mitigates the segregation of some alloying elements. The Ni 5 Gd phases accommodate a mass of Si and keep the Si content in the residual liquid phase low, which decreases the nucleation rate of M 6 C carbides. Then, the γ/M 2 C eutectic phases become the dominant ones at the final stage of the solidification process. Our results are useful in future optimization and processing research of Ni-Mo-Cr-Gd alloy for applications in molten salt reactors.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering