Abstract:The cooperative assembly of functional precursors with block copolymers (BCPs) is a powerful, general route to fabricate ordered mesoporous materials, but the precise tuning of the mesopore size generally requires trial and error to obtain the correct BCP template or appropriate swelling agent. Here, we demonstrate the ability to effectively modulate both expansion and contraction of the ordered cylindrical mesopores relative to those obtained from cooperatively assembled Pluronic F127, resol, and tetraethylorthosilicate. The two key physical parameters for the swelling agents are their hydrophobicity, as quantified by the octanol-water partition coefficient (Kow), and Hansen solubility parameters that describe the interactions of the solvent with the different components of the BCP template. Four low volatility solvents are examined that span a wide Kow with up to 90 wt % solvent relative to the Pluronic F127. Glycerol triacetate (Kow < 1) can decrease the average mesopore size from 5.9 to 4.8 nm due to segmental screening of the interactions in the Pluronic F127 to decrease chain stretching at intermediate loadings. A modest increase in mesopore size to 8.1 nm can be achieved with trimethylbenzene (TMB, Kow = 3.42). Dioctyl phthalate (DOP), which is slightly more hydrophobic (Kow = 8.1), is more effective than TMB at expanding the pore size (maximum: 13.5 nm) without loss of ordered structure. A more hydrophobic solvent, tris (2-ethylhexyl) trimellitate (Kow = 12.5), is less effective at increasing the pore size (maximum: 8.2 nm). The Hansen solubility parameters for DOP most closely match those of the hydrophobic segment in the Pluronic F217 template. We attribute this similarity, which is related to the solvent quality, to the improved efficacy of DOP in increasing the pore size. These results illustrate that both the Hansen solubility parameters (relative to the hydrophobic segment of the template) and relative hydrophobicity of the swelling agent determine the obtainable pore sizes in cooperatively assembled ordered mesoporous materials.

A simple organic–inorganic co-assembling route to pore-expanded ordered mesoporous carbons with 2-D hexagonal mesostructure

An Aqueous Cooperative Assembly Route to Synthesize Ordered Mesoporous Carbons with Controlled Structures and Morphology

A facile aqueous route tosynthesize highly ordered mesoporous carbons with open pore structures

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Facile Fabrication of Hierarchically Porous Carbonaceous Monoliths with Ordered Mesostructure Via an Organic Organic Self-Assembly

Control of Pore Size in Ordered Mesoporous Carbon-Silica by Hansen Solubility Parameters of Swelling Agent

Synthesis of Ordered Three-Dimensional Large-pore Mesoporous Silica and Its Replication to Ordered Nanoporous Carbon

Facile Synthesis of Hierarchically Ordered Porous Carbon Via in Situ Self-Assembly of Colloidal Polymer and Silica Spheres and Its Use As a Catalyst Support

Facile Synthesis of Ordered Mesoporous Carbons with High Thermal Stability by Self-Assembly of Resorcinol-Formaldehyde and Block Copolymers under Highly Acidic Conditions

Synthesis of Ordered Mesoporous Mgo/Carbon Composites by A One-Pot Assembly of Amphiphilic Triblock Copolymers

Preparation of Porous Carbons from Halloysite-Sucrose Mixtures

Synthesis of ordered small pore mesoporous silicates with tailorable pore structures and sizes by polyoxyethylene alkyl amine surfactant

Hierarchical Mesoporous Carbon/Silica Nanocomposites from Phenyl‐Bridged Organosilane

Highly Ordered Mesoporous Carbonaceous Frameworks from a Template of a Mixed Amphiphilic Triblock-Copolymer System of PEO-PPO-PEO and Reverse PPO-PEO-PPO.

Ordered Mesoporous Silicas And Carbons With Large Accessible Pores Templated From Amphiphilic Diblock Copolymer Poly(Ethylene Oxide)-B-Polystyrene

Ultra-large-pore mesoporous carbons templated from polyethylene oxide-b-polystyrene diblock copolymer by adding polystyrene homopolymer as a pore expander

Synthesis of Ordered Mesostructured Polymer–organosilica Composites by the Triconstituent Co-Assembly Method

Triconstituent Co-Assembly to Ordered Mesostructured Polymer-Silica and Carbon-Silica Nanocomposites and Large-Pore Mesoporous Carbons with High Surface Areas.

A Family of Highly Ordered Mesoporous Polymer Resin and Carbon Structures from Organic−Organic Self-Assembly

Growth of Single-Crystal Mesoporous Carbons with Im3̅m Symmetry

Anionic Surfactant Induced Mesophase Transformation to Synthesize Highly Ordered Large-Pore Mesoporous Silica Structures