Abstract:In this work, we studied the microstructure and mechanical properties of hot-pressed B4C, B4C + 5 wt% TiAl, and B4C + B + 5 wt% TiAl. The X-ray diffraction and Raman spectroscopy results showed that the addition of Ti–Al alone did not led to Al doping in B4C, and it did not reduce the degree of amorphization of B4C generated under high shear stresses. In contrast, the co-addition of Ti–Al and B resulted in both B and Al solid solutions in the B4C and effectively mitigated the amorphization of B4C. Electron probe microanalysis (EPMA) and energy dispersive X-ray spectroscopy (EDS) analyses suggested that the co-addition of Ti–Al and B promoted the interdiffusion of lightweight elements such as B, C, Al, Mg, and Si at high temperatures, resulting in a dense body with uniformly distributed second phase. The transmission electron microscopy (TEM) observations of the B4C + B + 5 wt% TiAl sample showed that a nano–core–shell structure with aggregated dislocations in the shells which was generated at TiB2 grains due to the segregation and dissolution-precipitation between TiB2 and B-rich boron carbide. The short-range ordered substitution of B and the disordered doping of Al in B4C led to lattice distortion and expansion, resulting in the formation of high-density defects, including stacking faults and nano-twins, improving the mechanical properties for B4C. The B4C + B + 5 wt% TiAl sample exhibits a combination of fascinating properties, including low density (2.52 g/cm3), high Vickers hardness (35.53 ± 0.83 GPa) and moderate fracture toughness (4.37 ± 0.35 MPa m1/2).

Effect of Al Addition on the Microstructures and Compression Properties of (ticxny–tib2)/ni Composites Fabricated by Combustion Synthesis and Hot Press

High pressure sintering behavior and mechanical properties of cBN-Ti 3Al and cBN-Ti 3Al-Al composite materials

Effect of Al content on impact resistance behavior of Al-Ti-B4C composite fabricated under air atmosphere

Effects of alloy elements (Mg, Zn) on the microstructure and mechanical properties of (TiC+TiB2)/Al composites

Microstructure and Mechanical Properties of TiB2-Al2O3 Composites

Microstructure and mechanical properties of TiB 2 -Al 2 O 3 composites

Compression properties and work-hardening behavior of the NiAl matrix composite reinforced with in situ TaC ceramic particulates

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Synthesis and Mechanical Properties of TiB2/Ti2AlN Composites Fabricated by Hot Pressing Sintering

Microstructure, Mechanical and Tribological Properties of NiAl Matrix Composites with Addition of BaO/TiO2 Binary Oxides

Mechanical Alloying and Spark Plasma Sintering of Ni-Al-Ti-B Powders for Fabricating Nanocrystailine (Tib+tib2)/ni-3(Al, Ti) Composite

Effect of Ni Additive on the Microstructure of TiB2-Cu Matrix Composites

Effect of nano-Al2O3 addition on microstructure and mechanical properties of Ti2AlNb-based composites prepared by powder metallurgy

Microstructure, mechanical properties and thermal shock behavior of h-BN–AlN ceramic composites prepared by combustion synthesis

Study on Microstructure of NiAl Matrix High Temperature Lubricating Composites Containing BaO/TiO2 Metallic Oxide

In Situ Synthesis and Properties of Ti<sub>3</sub>AlC<sub>2</sub>/TiB<sub>2</sub> Composites

Effects of Forming Conditions and TiC–TiB 2 Contents on the Microstructures of Self-Propagating High-Temperature Synthesized NiAl–TiC–TiB 2 Composites

The effect of B and Ti–Al intermetallics additions on the microstructure and mechanical properties of hot-pressed B4C

Effects of TiAl Alloy as a Binder on Cubic Boron Nitride Composites

Microstructure, Mechanical Properties and High Temperature Tribological Behavior of NiAl-based Composites

Microstructures, Densification and Mechanical Properties of TiC–Al2O3–Al Composite by Field-Activated Combustion Synthesis