Energy transfer mechanisms in Tb 3+ , Yb 3+ codoped Y 2 O 3 downconversion phosphor

xinxin yang,haohong chen,zhijun zhang,jingtai zhao,xiaoyan zeng,junlin yuan

DOI: https://doi.org/10.1088/0022-3727/41/10/105406

2008-01-01

Abstract:Tb(3+) and Yb(3+) co-activated luminescent material that can cut one photon of around 483 nm into two NIR photons of around 1000 nm could be used as a downconversion luminescent convertor in front of crystalline silicon solar cell panels to reduce thermalization loss of the solar cell. The Tb(3+) -> Yb(3+) energy transfer mechanisms in the UV-blue region in Y(2)O(3) phosphor were studied by PL excitation spectra and time-resolved luminescence, from which the charge transfer mechanism and the cooperative transfer mechanism were identified. Tb(3+) ions in the 4f(7)5d(1) state relax down to the (5)D(4) level and cooperatively transfer energy to two Yb(3+) ions, which is followed by the emission of two photons (lambda similar to 1000 nm). It was found in the (Y(0.79)Tb(0.01)Yb(0.20))(2)O(3) sample that 37% of the Tb(3+) ions at the (5)D(4) level transfer energy to two neighbouring Yb(3+) ions by the cooperative energy transfer mechanism Tb(3+) ((5)D(4)) -> 2Yb(3+) ((2)F(5/2)). Unfortunately, the high Yb(3+) concentration leads to severe concentration quenching that significantly reduces the external quantum efficiency. Moreover, the energy of the Tb3+ 4f(7)5d(1) state can also be lost non-radiatively or transferred to the Yb3+ (2)F(5/2) state via the charge transfer state Tb(4+)-Yb(2+). In conclusion, RE(3+) (RE = Ce, Pr, Tb) with strong absorption in the UV region is not an appropriate sensitizer of Tb(3+) in Tb(3+)-Yb(3+) codoped downconversion phosphor.