Preparation and luminescence of down-conversion material β-NaYF4:Tb3+, Yb3+

Guicheng Jiang,Xiantao Wei,LinXiang Wang,Xiaochun Wang,Yonghu CHEN,Min YIN

DOI: https://doi.org/10.3964/j.issn.1000-0593(2011)02-0331-04

2011-01-01

Spectroscopy and spectral analysis

Abstract:NaYF4 : Tb3+, Yb3+ down-conversion (DC) phosphors were synthesized by hydrothermal method. X-ray diffraction (XRD), photoluminescence (PL) and photoluminescence excitation (PLE) spectra were used to characterize the samples. Experiment results revealed that samples of NaYF4 : Tb3+, Yb3+ crystallized in hexagonal shape without cubic shape. When the doping concentration of Tb3+ and Yb3+ was altered, the lattice structure of samples did not change, indicating that the Tb3+ and Yb3+ ions are completely dissolved in the NaYF4 host lattice by substitution for the Y3+. The emission from D-5(4)-> F-7(6) (489 nm), D-5(4)-> F-7(5)(542 nm), D-5(4)-> F-7(4)(584 nm), and D-5(4)-> F-7(3)(619 nm) of Tb3+ ions was observed, in which the dominant emission was at 542 nm. With single Tb3+ doping, no near-infrared (NIR) emission was observed under excitation of 355 nm pulsed laser. However, while with Tb3+ and Yb3+ codoping, the NIR emission at around 950 similar to 1 100 nm from Yb3+ (F-2(5/2)-> F-2(7/2)) was observed under the same excitation. The dependence of the visible and NIR-emissions on Yb3+ doping concentration has been investigated. These results show that there is energy transfer process between Tb3+ and Yb3+. Furthermore, it is a possible DC process through cooperative energy transfer from Tb3+ to Yb3+. When the doping concentration is 1% mol Tb3+ and 6% mol Yb3+ respectively, the intensity of NIR emission reaches its strongest.