The effect of Gd on the microstructure and electrochemical properties of Mg-Ni-based alloys
Weilong Chen,Jianchun Sha,Lianhui Li,Jiaxin Bao,Yiqiang Yang,Mingliang Qiao,Jie Tian,Zhiqiang Zhang
DOI: https://doi.org/10.1016/j.jallcom.2024.173638
IF: 6.2
2024-01-25
Journal of Alloys and Compounds
Abstract:The Mg-Ni-based alloys have been extensively investigated as negative electrode materials in Nickel-Metal Hydride (Ni-MH) batteries. In this work, two Mg-Ni-based samples (Mg 71 Ni 29 and Mg 72.6 Ni 25.3 Gd 1.1 ) were prepared by means of melting. The X-ray diffraction (XRD), scanning electron microscope (SEM), galvanostatic charging/ discharging and other electrochemical measurements were used for the investigation. The results show that the Mg 71 Ni 29 and Mg 72.6 Ni 25.3 Gd 1.1 alloys include the characteristic peaks of Mg 2 Ni and the less strong characteristic peaks of Mg and MgNi 2 phases. The diffraction peak of the major phase Mg 2 Ni of the Mg 72.6 Ni 25.3 Gd 1.1 alloy is shifted to a small angle and its unit cell volume increases. With the addition of Gd, the alloy electrodes exhibits better cycling stability. After 50 charge/ discharge cycles, the capacity retention rate of the alloy electrode increase from 16% (Mg 71 Ni 29 ) to 22% (Mg 72.6 Ni 25.3 Gd 1.1 ). However, the maximum discharge capacity of the alloy electrode decrease from 134.3 mAh/g (Mg 71 Ni 29 ) to 91.9 mAh/g (Mg 72.6 Ni 25.3 Gd 1.1 ). The Mg 72.6 Ni 25.3 Gd 1.1 alloy possess lower limiting current density I L and exhibit relatively high corrosion resistance against the alkaline solution. After Gd doping, the charge transfer capacity of the Mg 72.6 Ni 25.3 Gd 1.1 alloy surface is increased.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering