Abstract:0.05–0.15 mm-thick ultra-thin grain-oriented silicon steel sheets were successfully produced by a novel processing route including strip casting, hot rolling, normalizing, two-stage cold rolling with intermediate annealing, primary recrystallization annealing and secondary recrystallization annealing. The evolutions of microstructure, texture and inhibitor along the processing were briefly investigated. The results showed that the initial Goss orientation originated due to the heterogenous nucleation of δ-ferrite grains during solidification. Because of the lack of shear deformation, only a few Goss grains were observed in the hot rolled sheet. After the first cold rolling and intermediate annealing, Goss texture was enhanced and distributed in the whole thickness. A small number of Goss grains having a high fraction of high energy boundaries exhibited in the primary recrystallization annealed sheet. A large number of fine and dispersed MnS and AlN and a few co-precipitates MnS and AlN with the size range of 10–70 nm were also observed. Interestingly, a well-developed secondary recrystallization microstructure characterized by 10–60 mm grains and a sharp Goss texture were finally produced in the 0.05–0.15 mm-thick ultra-thin sheets. A magnetic induction B8 of 1.72–1.84 T was obtained. Another new finding was that a few {2 3 0}〈0 0 1〉 and {2 1 0}〈1 2 7〉 grains also can grow up abnormally because of the high fraction of high energy boundaries and the size and number advantage, respectively. These non-Goss grains finally deteriorated the magnetic properties of the ultra-thin sheets. In addition, low surface energies of {hk0} planes may also contribute to the abnormal growth of Goss, {2 3 0}〈0 0 1〉 and {2 1 0}〈1 2 7〉 grains.

Sharp Goss Orientation and Large Magnetostriction in the Rolled Columnar-Grained Fe–Ga Alloys

Retaining the (001) Orientation from Initial Columnar Grains and Magnetostriction in Binary Fe-Ga Alloy Sheets

Secondary Recrystallization Behavior in the Rolled Columnar-Grained Fe–Ga Alloys

Intermediate Annealing of Warm-rolled Sheets and Its Influence on the Texture Evolution in the Rolled Columnar-grained Fe-Ga Alloys

Secondary recrystallization behavior in magnetostrictive Fe-Ga thin sheets induced by nano-sized composite precipitates

Rapid Secondary Recrystallization of the Goss Texture in Fe81Ga19 Sheets Using Nanosized NbC Particles

Secondary recrystallization induced by composite precipitates in magnetostrictive Fe-Ga alloy thin sheet

Large-scale First-Principles Determination of Anisotropic Mechanical Properties of Magnetostrictive Fe–Ga Alloys

Enhanced magnetostriction of rolled (Fe81Ga19)99.93Tb0.07 thin sheet by synergy strategy of secondary recrystallization and trace Tb-doping

Inhibition Force of Precipitates for Promoting Abnormal Grain Growth in Magnetostrictive Fe83Ga17-(B,NbC) Alloy Sheets

Goss Texture Evolution in a Grain-Oriented Fe-6.5wt%Si Steel Processed by Strip-Casting

Microstructure and Magnetostrictive Performance of NbC-doped <100> Oriented Fe-Ga Alloys

Ultra-thin grain-oriented silicon steel sheet fabricated by a novel way: Twin-roll strip casting and two-stage cold rolling

Structural Origin For The Local Strong Anisotropy In Melt-Spun Fe-Ga-Tb: Tetragonal Nanoparticles

Improved magnetostriction in Galfenol alloys by aligning crystal growth direction along easy magnetization axis

Understanding Strong Magnetostriction in Fe100−xGax Alloys

Large magnetostriction in directionally solidified FeGa and FeGaAl alloys

Morphology evolution and enhanced magnetostriction of (Fe0.81Ga0.19)99.9Tb0.1 crystals prepared by liquid metal cooling Bridgman directional solidification

Improved magnetostriction in cold-rolled and annealed Mn50Fe50 alloy

Deformation mechanism, orientation evolution and mechanical properties of annealed cross-rolled Mg-Zn-Zr-Y-Gd sheet during tension