Suzuki segregation in Co–Ni-based superalloy at 973K: An experimental and computational study by phase-field simulation
yuichiro koizumi,takeshi nukaya,s suzuki,shingo kurosu,yunping li,hiroaki matsumoto,kazuhisa sato,yuji tanaka,akihiko chiba
DOI: https://doi.org/10.1016/j.actamat.2012.01.054
IF: 9.4
2012-01-01
Acta Materialia
Abstract:Suzuki segregation in Co–Ni-based superalloys is of longstanding interest. In this study, the development of widely extended stacking fault (SF) ribbons was confirmed in a Co–Ni-based superalloy aged at 973K after deformation at room temperature, which supports the decrease in stacking fault energy (SFE) due to Suzuki segregation. In addition, the plastic deformation behaviors of Co–Ni-based superalloys with various Nb contents up to 3wt.% were investigated focusing on the effect of Nb addition on dynamic strain-aging by Suzuki segregation. The negative strain-rate dependence of flow stress due to dynamic strain-aging became more significant with increasing Nb content; however, attempts to detect segregating elements by scanning transmission electron microscopy and energy-dispersive spectroscopy analysis were not successful. A phase-field simulation of Suzuki segregation suggested strong Ni depletion with segregation of Cr and Mo atoms at the SF, and the SFE can become negative as a consequence of the segregation. This agrees with the experimentally observed formation of wide SFs by the aging at 973K after cold deformation. It is also suggested that Nb atoms are strongly depleted at SFs, and a small amount of Nb addition dramatically enhances Cr segregation, resulting in further decreases in the SFE, which is probably responsible for the observed enhancement of dynamic strain-aging by Nb addition. In addition, the local structural changes, such as short-range ordering and/or an in-plane ordering, accompanying the segregation were discussed as possible additional mechanisms for strain-aging enhancement.