Abstract:Amorphous SiBCN ceramics are a unique class of structure materials with potential applicationsas high-temperature heat-resistant structural components owing to their combination of special structure and properties of low specific weight, high specific strength and excellent damage tolerance at elevated temperatures. However, it is still in need for further mechanical properties improvements for actual demands by rational co-design of architecture and chemistry as well as understanding the basic features of morphological/microstructural evolution and failure behavior. Thus in this attempt, to target the dense amorphous Si2ByC2N (y=1.5～4) monoliths with high mechanical properties, an attractive way of combinatorial mechanical alloying and high-pressure sintering technique (1000 oC/3～5 GPa/30 min) was proposed using elemental powders of graphite, hexagonal BN, cubic Si and boron as raw materials. The sintering pressure induced microstructural evolution, phase transformation and thermal stability have been investigated by XRD, SEM, TEM and TG measurements, and mechanical performance, especially the fracture behavior was also discussed in details. Results clearly presented that an increase in sintering pressure promoted the phase transformation of completely amorphous matrix to a hybrid structure of substantial amorphous phases and few nanocrystals of metal c-Si and/or t-BN(C) for some monoliths, implying boron-content depending phase composition. High-pressure sintering effectively promoted the densification leading to free volume annihilation and the river-like fracture morphology occurrence. A monotonous increase of the bulk density, nano hardness and Young's modulus as a function of the sintering pressure was observed. Under the same sintering conditions, the increase in boron content weakened the mechanical properties and thermal stability of the amorphous Si2ByC2N (y=1.5～4) monoliths. Dense amorphous Si2B1.5C2N monoliths consolidated at 1000 oC/5 GPa/30 min showed the best performance with the bulk density, nano hardness and Young's modulus obtaining at 2.69 g/cm3, 33.6±2.2 GPa and 414.2±16.5 GPa, respectively.

Microstructure, Oxidation and Thermal Shock Resistance of Graphene Reinforced Sibcn Ceramics

Spark plasma sintering and toughening of graphene platelets reinforced SiBCN nanocomposites

Enhanced Mechanical Properties and Thermal Shock Resistance of Si2BC3N Ceramics with SiC Coated MWCNTs

Ablation behavior of graphene reinforced SiBCN ceramics in an oxyacetylene combustion flame

Effects of Zr and chopped C fiber on microstructure and mechanical properties of SiBCN ceramics

Fabrication of Dense SiBCN Monolith at a Lower Temperature Andits High-Temperature Performance

Enhanced Thermal Shock and Oxidation Resistance of Si2BC3N Ceramics Through MWCNTs Incorporation

Enhanced Mechanical Properties, Thermal Shock Resistance and Oxidation Resistance of Si2BC3N Ceramics with Zr-Al Addition

Processing and Characterization of SiB0.5C1.5N0.5 Produced by Mechanical Alloying and Subsequent Spark Plasma Sintering

Mechanical properties and thermal shock resistance of Si2BC3N ceramics with ternary Al4SiC4 additive

Microstructural Features and Properties of the Nano-Crystalline SiC/BN(C) Composite Ceramic Prepared from the Mechanically Alloyed SiBCN Powder

Microstructural evolution and mechanical performance of high-pressure sintered dense amorphous SiBCN monoliths

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Microstructures, Mechanical Properties and Oxidation Resistance of Sibcn Ceramics with the Addition of Mgo, Zro2 and Sio2 (mzs) As Sintering Additives

Effects of graphite flake diameter on mechanical properties and thermal shock behavior of ZrB2-nanoSiC-graphite ceramics

Cyclic thermal shock behaviors of carbon fibers reinforced SiCN ceramics with bio-inspired Bouligand-like architectures

Effect of boron content on the microstructure and electromagnetic properties of SiBCN ceramics

Preparation, Microstructures, Mechanical Properties and Oxidation Resistance of SiBCN/ZrB2–ZrN Ceramics by Reactive Hot Pressing

Effect of Si/C Ratio and Their Content on the Microstructure and Properties of Si–B–C–N Ceramics Prepared by Spark Plasma Sintering Techniques

Cyclic thermal shock behaviors of carbon fibers reinforced SiCN ceramics with architectures

Electrostatic Assembly Preparation of High-Toughness Zirconium Diboride-Based Ceramic Composites with Enhanced Thermal Shock Resistance Performance