Preparation and Properties of BaTiO3 Ceramics by Low Temperature Cold Sintering
Wei Tingting,Xu Huarui,Zhu Guisheng,Long Shenfeng,Zhang Xiuyun,Zhao Yunyun,Jiang Xupeng,Song Jinjie,Guo Ningjie,Gong Yipeng
DOI: https://doi.org/10.15541/jim20220115
2022-01-01
Abstract:Preparation of ceramics by cold sintering process has attracted great attention, and some progress has been made in the preparation of BaTiO3 ceramics. In order to improve the performance of cold sintered BaTiO3 ceramics, BaTiO3 powder with good dispersion, particle size of 100 nm and tetragonality (crystal parameter c/a of 1.0085) was prepared by hydrothermal method, and then the powder was hydrothermally activated at 100 degrees C for 1 h with 0.1 mol/L acetic acid. Dense BaTiO3 ceramics were prepared by the Cold Sintering Process at 400 degrees C, under a uniaxial pressure of 350 MPa for 1 h using 10% Ba(OH)(2)center dot 8H(2)O (in mass) as flux. The as-prepared ceramic pellets were further annealed at 600 degrees C for 0.5 h. In the end, BaTiO3 ceramic sample obtained excellent characteristics with relative density of 96.62%, grain size of 180 nm, dielectric constant (epsilon(r)) of 2836, and dielectric loss (tan delta) of 0.03. An amorphous titanium layer is formed on the surface of the highly active powder after acetic acid treatment, which effectively promotes the densification of ceramics, inhibits the formation of impurity phases and grain growth, improves the dielectric properties, greatly improves the dielectric dispersion phenomenon of cold sintered BaTiO3 ceramics, and realizes the low temperature cold sintering of BaTiO3 ceramics.