Effects of Nd-ions doping on the phase structure and electrical properties of PSN-PMN-PT ceramics
Yifei Chen,Feifei Guo,Min Wang,Hongqiao Zhou,Jianjin Gao,Wei Long,Zengzhe Xi
DOI: https://doi.org/10.1007/s10853-024-10185-7
IF: 4.5
2024-09-23
Journal of Materials Science
Abstract:The 0.29PSN-0.36PMN-0.35PT: x mol Nd 2 O 3 ( x = 0, 0.01, 0.015, 0.02, 0.025, and 0.03) piezoelectric ceramics are fabricated manufactured through the high-temperature sintering. Nd 3+ doping significantly enhanced the piezoelectric and dielectric properties of PSN-PMN-PT, with the ceramic containing 0.025 mol Nd 3+ exhibiting the optimal performance: d 33 = 890 pC N −1 , ɛ r = 5735, d 33 * = 1094 pm V −1 , E c = 4.32 kV cm −1 , T m = 136 °C, and P r = 4.32 μC cm −2 . Phase structure analysis and Rayleigh analysis results show that the excellent dielectric and piezoelectric responses of the ceramic are mainly due to the synergistic effect of MPB and the significant improvement of nano-scale local structural heterogeneity. Moreover, the variation rate of d 33 remained as low as 5% in the temperature range from room temperature to 120 °C. These comprehensive findings demonstrate that PSN-PMN-PT: 0.025 mol Nd 2 O 3 ceramics excel in both their piezoelectric capabilities and thermal stability, thus rendering it an attractive material for high sensitivity sensor.
materials science, multidisciplinary