Abstract:The inhibition power of two Schiff bases on carbon steel corrosion in 1 M HCl and 0.5 M H2SO4 solutions has been investigated using weight loss, Tafel polarization, and electrochemical impedance spectroscopy techniques. The results revealed that increasing the concentration of inhibitors in acidic solutions led to a higher inhibition efficiency. The inhibition power of two Schiff bases on carbon steel corrosion in 1 M HCl and 0.5 M H2SO4 solutions has been investigated using weight loss, Tafel polarization, and electrochemical impedance spectroscopy techniques. The results revealed that increasing the concentration of inhibitors in acidic solutions led to a higher inhibition efficiency. The polarization curves indicated that the Schiff bases acted as mixed inhibitors, affecting both the cathodic and anodic reactions. The adsorption of the inhibitors on the carbon steel surface followed the Langmuir adsorption isotherm, and various adsorption isotherm parameters such as Kads, ΔGads, ΔHads, and ΔSads were determined at room temperature. Furthermore, the effect of temperature on the inhibitors′ performance was examined within the range of 25–45 °C. The corrosion‐related activation energy, pre‐exponential factor (k), activation enthalpy, and entropy were calculated to assess the inhibitors′ behavior. Scanning electron microscopy (SEM) was employed to examine some carbon steel samples, revealing differences in inhibition efficiency attributed to the inhibitors′ chemical structure. The results highlighted the highest inhibition efficiency in H2SO4 medium at 93.4 %, with a corresponding free energy of 39.51 KJ/mol indicating physical‐chemical adsorption of inhibitor molecules. Furthermore, an enthalpy value of −40.6 KJ/mol suggested an exothermic inhibitor absorption process. The findings are presented and discussed in detail.

Inhibition effect of potassium iodide on metals in hydrochloric acid solution

Experimental and Theoretical Investigation of 1-Hexyl-3-methylimidazolium Iodide As a Corrosion Inhibitor for Mild Steel in HCl Environment

Inhibition Synergism Between Alkyl Imidazoline and Potassium Iodide on the Corrosion of Carbon Steel in Citric Acid Solution

Inhibition Effects of L−and L2on Stress Corrosion Cracking of Stainless Steel in Acidic Chloride Solutions

Synergistic effect of potassium iodide and sodium dodecyl sulfonate on the corrosion inhibition of carbon steel in HCl medium: a combined experimental and theoretical investigation

Inhibitive Effect of an Onium Compound on the Dissolution of Steel in Hydrochloric Acid

Synergistic inhibition effect of walnut green husk extract and potassium iodide on the corrosion of cold rolled steel in trichloroacetic acid solution

Bio-based ionic liquid as a corrosion inhibitor for mild steel in 5% HCl solution: Experimental and theoretical investigation

Inhibition Effect of Calcium Tartrate on the Corrosion of Pure Aluminum in an Alkaline Solution

Benzalkonium chloride/titanium dioxide as an effective corrosion inhibitor for carbon steel in a sulfuric acid solution

SYNERGISTIC CORROSION INHIBITION ACTIVITY OF THE CHICORIUMINTYBUS EXTRACT AND IODIDE IONS FOR MILD STEEL IN ACIDIC MEDIA

Experimental and Theoretical Studies of the Corrosion Inhibition Performance of a Quaternary Phosphonium-Based Ionic Liquid for Mild Steel in HCl Medium

Inhibiting Effect of Ionic Liquids on the Corrosion of Mild Steel in H2S and HCl Solution

Effect of Cation Types on the Steel Corrosion Inhibition Behavior of Calcined Layered Double Hydroxides in Saturated Calcium Hydroxide Solution

Electrochemical corrosion behavior of stainless steel in dilute hydrochloric acid media containing SO4 2- ions

Corrosion Inhibition of Carbon Steel by Some Schiff Base Compounds in HCl and H2SO4 Solutions

Corrosion inhibition of aluminum in sodium hydroxide solutions using some inorganic anions

Effect of Inhibitors on the Critical Pitting Temperature of the High-Entropy Alloy Co1.5CrFeNi1.5Ti0.5Mo0.1

Inhibition Effect and Mechanism of Tin on the Active Dissolution of Tin-Containing 430LX Ferritic Stainless Steel

Synergistic effect of KI on the corrosion inhibition of a poly(diallylammonium chloride)-based cyclocopolymer containing bis-cationic motifs for mild steel corrosion in 20% formic acid

The effect of N and S ratios in N, S co-doped carbon dot inhibitor on metal protection in 1 M HCl solution