An investigation on the effect of heat input to wear behavior and corrosion-cavitation erosion mechanism of Hastelloy C-276 coating by cold metal transfer
T. Zhao,R. Wang,H.F. Zhang,C.H. Zhang,S. Zhang,H.T. Chen,C.L. Wu
DOI: https://doi.org/10.1016/j.matchar.2024.113819
IF: 4.537
2024-03-17
Materials Characterization
Abstract:Cold metal transfer (CMT) technology based on wire-arc manufacturing has attracted wide attention because of its advantages of high manufacturing efficiency, low heat input ( HI ) and near-net-shape. In this study, a CMT-Hastelloy C-276 superalloy surface modification coating by optimizing HI is used to solve the problem of premature failure of key over-flow components of stainless steel in marine engineering. When the HI is increased from 269 J/mm to 358 J/mm, the serious cavitation erosion (CE) damage caused by pore defects and excessive residual tensile stress due to excessive low HI of Hastelloy C-276 coating can be avoid, which is attributed to the effective Orowan strengthening and high proportion of low angle grain bounds (LAGBs: 70.2%). In addition, high contents of Cr, Mo and W elements can promote it's passivation film to maintain excellent self-healing ability during CE to provide continuous and stable protection effect ( R ct = 75.68 kΩ·cm 2 ) in the 3.5 wt% NaCl artificial seawater. Therefore, even after 10 h-CE, it still maintains the highest corrosion resistance from both of the thermodynamic ( E corr = −193.5 ± 3.6 mV) and kinetic perspective ( I corr = 69.3 ± 3.1 μA·cm −2 ) and has the lowest mean depth erosion rates ( MDER , 0.94 ± 0.07 μm/h). However, further increase of HI will cause coarsing of grains (89.6 ± 2.7 μm → 342.8 ± 9.7 μm), excessive precipitation of brittle Mo-rich p phase and excessive dilution of elements from the substrate, resulting in changes in the wear mechanism and deterioration of strength and corrosion resistance. Moreover, the potential of zero charge ( PZC ) measurements and Mott-Schottky ( M-S ) test confirmed the decreasing trend of the repulsive ability to Cl ions ( ΔE = 0.58 V) and the increased ion doping concentration ( N D = 5.94 ± 0.02 × 10 22 cm −3 ) of the weakened n-type passivation films. The optimal combination of wear resistance, corrosion resistance and CE resistance of Hastelloy C-276 coating is obtained by regulating HI , which can lay a theoretical foundation for the related production and application of marine engineering.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing