Abstract:Vibrational sum frequency generation (VSFG) spectroscopy was used in conjunction with steady-state IR spectroscopy, atomic force microscopy (AFM), and spectroscopic ellipsometry to characterize organic semiconductor thin films that were vapor deposited on silica- and trimethoxy(octadecyl)silane (ODTMS)-functionalized silica surfaces. The growth of perylene derivative N,N'-dioctyl-3,4,9,10-perylenedicarboximide (PTCDI-C(8)) was found to proceed differently on simple glass slides relative to that of native oxide on silicon and fused quartz slides. VSFG was applied to these samples to isolate structural changes that occurred specifically at the buried interface between the organic semiconductor and the silica dielectric upon thermal annealing. A model was introduced to globally fit the imide carbonyl symmetric and asymmetric interfacial spectra that included contributions from both inner and outer interfaces. The fits to the VSFG data and AFM topographic images revealed significant reordering at the outer interface on all substrates upon thermal annealing. Within the model, the spectroscopic data reported that the inner interfacial PTCDI-C(8) monolayer reoriented to a more reclined phase on bare substrates after annealing but remained essentially unchanged on ODTMS monolayers. Electrical characterization of PTCDI-C(8) field-effect transistors indicated that electron mobilities were higher on bare substrate devices but could be improved by a factor of 2 on both surface types by thermal annealing. The mobility effects were attributed to the annealing-driven coalescence of PTCDI-C(8) grain boundaries. Consistent with previous structural reports, the molecular rearrangements of the first monolayer of PTCDI-C(8) on bare substrates that were reported by VSFG spectroscopy had a noticeable impact on the device performance.

Abrupt Change on the Wettability of Vapor-Deposited Thin Silane Film Upon Evaporative Drying and Annealing

Stabilizing the Wettability of Initiated Chemical Vapor Deposited (icvd) Polydivinylbenzene Thin Films by Thermal Annealing

Friction and Wear Studies of Octadecyltrichlorosilane SAM on Silicon

Improved Hydrophobicity of Vapor Coated Chlorosilane Self Assembled Monolayers Using Evaporative Drying of Solvent and Annealing

Fabrication of pillar-array superhydrophobic silicon surface and thermodynamic analysis on the wetting state transition

Natural Hydrophobicity and Reversible Wettability Conversion of Flat Anatase TiO₂ Thin Film.

Topographical and Performance Characterization of OTS Self-assembled Monolayer on Chemically Textured Silicon Surfaces

Wettability behavior of DTMS modified SiO 2 : Experimental and molecular dynamics study

Study on Structural, Optical and Hydrophilic Properties of FTO/TiO2 Tandem Thin Film Prepared by Aerosol-Assisted Chemical Vapor Deposition Method

Surface Orientation and Temperature Effects on the Interaction of Silicon with Water: Molecular Dynamics Simulations Using ReaxFF Reactive Force Field.

High-Pressure Water-Vapor Annealing for Enhancement of A-Si:H Film Passivation of Silicon Surface

Analysing the surface morphology of annealed FTO/ZnS bilayer films: stereometric, fractal, and wettability approaches

CHARACTERIZATION OF OCTADECYLTRICHLOROSILANE SELF-ASSEMBLED MULTILAYERS ON PYREX GLASS

Thermal Stability of Octadecyltrichlorosilane and Perfluorooctyltriethoxysilane Monolayers on SiO2

Tailoring the wettability of nanocrystalline TiO 2 films

Surface chemistry and annealing-driven interfacial changes in organic semiconducting thin films on silica surfaces

Nanoscale Analysis of Surface Modifications on Silanized Glass: Wettability Alteration and Long-Term Stability

Oxygen Vacancy Induced Structure Change and Interface Reaction in HfO2 Films on Native SiO2/Si Substrate

Effect of Surface Morphology on Wettability Conversion

Tribological Properties of OTS Self-Assembled Monolayers

Friction Properties of OTS SAMs and Silicon Surface under Water Lubrication