Abstract:Calcium looping cycle for post-combustion CO2 capture has gained increasing attention worldwide. However, CaO-based sorbents derived from natural sources for calcium looping cycle experience rapid loss of capacity during high-temperature cyclic carbonation/calcination reactions. Synthesizing sintering-resistant CaO-based sorbents by adding a support material has been extensively studied as an effective method of combating the problem. The support material in the synthetic sorbents plays an important role in retaining the capacity, and various support materials have been tested in the literature. In practical reactors, sulfur is present and it has been reported that sulfation of sorbents will also reduce the CO2 capture capacity. However, thus far, it is not clear whether/how support material would affect sulfation of sorbents and, thus, CO2 capture. In this paper, four different support materials, such as Ca2MnO4, La2O3, Ca12Al14O33, and MgO, were studied. The cyclic CO2 capture performance of the synthetic sorbents made from CaO and the support materials were investigated in detail, in the presence of SO2 and steam. The results showed that a mass ratio of 20-25% support material would be optimum for synthesizing sorbents with high cyclic CO2 capture capacity, and Ca12Al14O33 and MgO seem to be more effective than Ca2MnO4 and La2O3. The 80:20 wt % CaO/MgO synthetic sorbent achieved the highest CO2 capture capacity under ideal conditions over 100 cycles. However, the CaO/MgO sorbent had a strong affinity to SO2 capture during cyclic reactions, especially in the presence of steam. Under realistic conditions (i.e., both SO2 and steam are present during carbonation), the CaO/MgO sorbent showed the highest cumulative SO2 capture capacity, whereas the CaO/Ca12Al14O33 sorbent obtained the highest CO2 capture capacity after 10 cycles. The smaller average crystallite size of MgO in the sorbent was responsible for the strong SO2 affinity of the CaO/MgO sorbent as well as its stable cyclic CO2 capture abilities under ideal conditions.

Removal of Co2 by Cao/Mgo and Cao/Ca9al6o18 in the Presence of So2

Properties of a Nano CaO/Al2O3 CO2 Sorbent

Properties of SiO_2 Coated Nano SiO_2/CaCO_3 Sorbents by Precipitation Method

Calcination–carbonation Durability of Nano CaCO3 Doped with Li2SO4

Properties of Ca-Base Co2 Sorbent Using Ca(Oh)(2) As Precursor

Properties of a Nano CaO/Al<sub>2</sub>O<sub>3</sub>CO<sub>2</sub>Sorbent

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Characteristics of MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Effect of Support Material on Carbonation and Sulfation of Synthetic Cao-Based Sorbents in Calcium Looping Cycle

Enhanced cyclic stability of CO 2 adsorption capacity of CaO-based sorbents using La 2 O 3 or Ca 12 Al 14 O 33 as additives

SGCS-made Ultrafine CaO/Al2O3 Sorbent for Cyclic CO2 Capture

Studies on CO2 uptake by CaO/Ca3Al2O6 sorbent in calcium looping cycles

Efficient MgO-doped CaO sorbent pellets for high temperature CO2 capture

Cyclic Reaction Characters of Novel CaO/MgO High Temperature CO2 Sorbents

Effects of Drying Methods on Wet Chemistry Synthesis of Al-Stabilized CaO Sorbents for Cyclic CO2 Capture

Wet Mixing Combustion Synthesis of CaO-based Sorbents for High Temperature Cyclic CO2 Capture

Effect of Preparation Temperature on Cyclic CO2 Capture and Multiple Carbonation−Calcination Cycles for a New Ca-Based CO2 Sorbent

Synthesis and Performance of a Nano Synthetic Ca-based Sorbent for High Temperature CO_2 Capture

Investigation on a Novel CaO–Y2O3 Sorbent for Efficient CO2 Mitigation

Development and performance of CaO/La2O3 sorbents during calcium looping cycles for CO2 capture