Abstract:CeO2/TiO2 and CeO2−WO3/TiO2 catalysts prepared by impregnation method assisted with ultrasonic energy were investigated on the selective catalytic reduction (SCR) of NOx (NO and NO2) by NH3. The catalytic activity of 10% CeO2/TiO2 (CeTi) was greatly enhanced by the addition of 6% WO3 in the broad temperature range of 200−500 °C, the promotion mechanism was proposed on basis of the results of in situ diffuse reflectance infrared transform spectroscopy (DRIFT). When NH3 was introduced into both catalysts preadsorbed with NO + O2, SCR would not proceed except for the reaction between NO2 and ammonia. For CeO2/TiO2 catalysts, coordinated NH3 linked to Lewis acid sites were the main adsorbed ammonia species. When NO + O2 was introduced, all the ammonia species consumed rapidly, indicating that these species could react with NOx effectively. Two different reaction routes, L-H mechanism at low temperature (<200 °C) and E-R mechanism at high temperatures (>200 °C), were presented for SCR reaction over CeO2/TiO2 catalyst. For CeO2−WO3/TiO2 catalysts, the Lewis acid sites on Ce4+ state could be converted to Brønsted acid sites due to the unsaturated coordination of Cen+ and Wn+ ions. When NO + O2 was introduced, the reaction proceeded more quickly than that on CeO2/TiO2. The reaction route mainly followed E-R mechanism in the temperature range investigated (150−350 °C) over CeO2−WO3/TiO2 catalysts. Tungstation was beneficial for the formation of Ce3+, which would influence the active sites of the catalyst and further change the mechanisms of SCR reaction. In this way, the cooperation of tungstation and the presence of Ce3+ state resulted in the better activity of CeO2−WO3/TiO2 compared to that of CeO2/TiO2.

Effect of different introduction methods of cerium and tin on the properties of titanium-based catalysts for the selective catalytic reduction of NO by NH3

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Comparative study of Ce-Nb-Ti oxide catalysts prepared by different methods for selective catalytic reduction of NO with NH3

Promotional Effects on NH3-SCR Performance of CeO2–SnO2 Catalysts Doped by TiO2: A Mechanism Study

Solid-phase impregnation promotes Ce doping in TiO2 for boosted denitration of CeO2/TiO2 catalysts

Promotional Effect Of Doping Sno2 Into Tio2 Over A Ceo2/Tio2 Catalyst For Selective Catalytic Reduction Of No By Nh3

Selective catalytic reduction of NO<sub>x</sub> with NH<sub>3</sub> over a novel Co-Ce-Ti catalyst

Promotional Effect of Ce on Iron-Based Catalysts for Selective Catalytic Reduction of NO with NH3

Effect of Ce Doping into V2O5-WO3/TiO2 Catalysts on the Selective Catalytic Reduction of NOx by NH3

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

Effect of Ti4+ and Sn4+ Co-Incorporation on the Catalytic Performance of CeO2-MnOx Catalyst for Low Temperature NH3-SCR

Effect of Metal Ions Doping (M = Ti4+, Sn4+) on the Catalytic Performance of MnOx/CeO2 Catalyst for Low Temperature Selective Catalytic Reduction of NO with NH3

Activity and Characterization of Ce–Mo–Ti Mixed Oxide Catalysts Prepared by a Homogeneous Precipitation Method for Selective Catalytic Reduction of NO with NH3

Promoting N-2 Selectivity of CeMnOx Catalyst by Supporting TiO2 in NH3-SCR Reaction

Superior Ce–Nb–Ti oxide catalysts for selective catalytic reduction of NO with NH3

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

The activity and characterization of CeO2-TiO2 catalysts prepared by the sol-gel method for selective catalytic reduction of NO with NH3.

Active Site of O2 and Its Improvement Mechanism over Ce-Ti Catalyst for NH3-SCR Reaction

Promotion effect of Ce and Ta co-doping on the NH3-SCR performance over V2O5/TiO2 catalyst

DRIFT Study on Cerium−Tungsten/Titiania Catalyst for Selective Catalytic Reduction of NOx with NH3

Mechanistic insight into the promoting effect of partial substitution of Mn by Ce on N2 selectivity of MnTiO catalyst for NH3-SCR of NO