Nanosize effects assisted synthesis of the high pressure metastable phase in ZrO2.

Quanjun Li,Huafang Zhang,Ran Liu,Bo Liu,Dongmei Li,Lirong Zheng,Jing Liu,Tian Cui,Bingbing Liu

DOI: https://doi.org/10.1039/c5nr07503c

IF: 6.7

2016-01-01

Nanoscale

Abstract:The size effects on the high pressure behaviors of monoclinic (MI) ZrO2 nanoparticles were studied using in situ high pressure synchrotron X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). A size-dependent phase transition behavior under high pressure was found in nanoscale ZrO2. The normal phase transition sequence of MI-orthorhombic I (OI)-orthorhombic II (OII) occurs in 100-300 nm ZrO2 nanoparticles, while only the transition of MI-OI exists in ultrafine similar to 5 nm ZrO2 nanoparticles up to the highest experimental pressure of similar to 52 GPa. This indicates that the size effects preclude the transition from the OI to the OII phase in similar to 5 nm nanoparticles. Upon decompression, the OII and OI phases are retained down to ambient pressure, respectively. This is the first observation of the pure OI phase ZrO2 under ambient conditions. The bulk moduli of the MI ZrO2 nanoparticles were determined to be B-0 = 192 (7) GPa for the 100-300 nm nanoparticles and B0 = 218 (12) GPa for the similar to 5 nm nanoparticles. We suggest that the significant high surface energy precludes the transition from the OI to the OII phase and the nanosize effects enhance the incompressibility in the ultrafine ZrO2 nanoparticles (similar to 5 nm). Our study indicates that this is a potential way of preparing novel nanomaterials with high pressure structures using nanosize effects.