Abstract:Hollow-structured SiO2, which comprises a void space inside a distinct shell with its intriguing physicochemical properties and huge potential, has been widely applied in many methanation catalysts. However, the common methods for preparing SiO2 hollow microspheres are cumbersome and time consuming. Highly uniform hollow nanoflowers, silica (SiO2) nanospheres with different sizes, were synthesised through a rapid, time-saving method known as flash nanoprecipitation. An assembling particle mechanism of the hollow structure of Mo–polydopamine complex was established and tetraethyl orthosilicate underwent uniform hydrolysis on the surface of the hierarchical structure. Spherical SiO2 samples with different morphologies were prepared as catalyst carriers, and Ni-based methanation catalysts were prepared using an impregnation method. Ni particles with size of 3 nm were successfully attached to the surface of MoDo–H–SiO2, while the particle sizes of Ni on CTS–MoDo–H–SiO2 was 7 nm. The small particles (3 nm) were found to significantly increase in size (20–50 nm), decrease by 90% in stability test with a weight hourly space velocity (WHSV) of 26,000 mL.g−1.h−1, which is detrimental to catalyst stability. However, the medium sized particles (7 nm) remained confined via a suitable interaction involving the support, thus displaying enhanced stability, with 100% CO conversion at 250 °C and no obviously decrease in stability test Although more active sites can be provided with smaller active metals, catalysts with small sized particles deactivate faster and to a larger extent than catalysts with medium sized particles. Thus, the smaller the particle size of the active component, the worse the stability.

Synthesis of Supported Ultrafine Non-Noble Subnanometer-Scale Metal Particles Derived from Metal-Organic Frameworks As Highly Efficient Heterogeneous Catalysts

Synthesis of Ultrafine and Highly Dispersed Metal Nanoparticles Confined in a Thioether-Containing Covalent Organic Framework and Their Catalytic Applications

Supported Ultrafine NiCo Bimetallic Alloy Nanoparticles Derived from Bimetal–Organic Frameworks: A Highly Active Catalyst for Furfuryl Alcohol Hydrogenation

Confinement of Ultrasmall Cu/ZnOx Nanoparticles in Metal-Organic Frameworks for Selective Methanol Synthesis from Catalytic Hydrogenation of CO2

In Situ Synthesis of Core–Shell Pt–Cu Frame@Metal–Organic Frameworks As Multifunctional Catalysts for Hydrogenation Reaction

General Immobilization of Ultrafine Alloyed Nanoparticles within Metal–Organic Frameworks with High Loadings for Advanced Synergetic Catalysis

A seed-mediated approach to the general and mild synthesis of non-noble metal nanoparticles stabilized by a metal–organic framework for highly efficient catalysis

Facile Synthesis of Highly Dispersed and Well‐Alloyed Bimetallic Nanoparticles on Oxide Support

Ultrasmall Au Nanoparticles Embedded In 2d Mixed-Ligand Metal-Organic Framework Nanosheets Exhibiting Highly Efficient And Size-Selective Catalysis

Up-scaled Synthesis of Flower-Like SiO2 Microspheres Via Continuous Flash Nanoprecipitation and Their Application As a Catalyst Support

Synthesis of Carbon-Supported Sub-2 Nanometer Bimetallic Catalysts by Strong Metal–sulfur Interaction

Immobilization of Metal-Organic Framework Nanocrystals for Advanced Design of Supported Nanocatalysts.

Dynamically modulated synthesis of hollow metal-organic frameworks for selective hydrogenation reactions

Metal−organic Framework Encapsulated Pd Nanoparticles: Towards Advanced Heterogeneous Catalysts

Ultrafine platinum/iron oxide nanoconjugates confined in silica nanoshells for highly durable catalytic oxidation

Aerosol Spray Drying Guided Synthesis of Ultrasmall Alloyed Bimetallic Nanoparticles Supported on Silica for Catalytic Semihydrogenation

Metal–Organic Framework‐Mediated Synthesis in Catalysis

High-Temperature Synthesis of Carbon-Supported Bimetallic Nanocluster Catalysts by Enlarging the Interparticle Distance

A Sulfur-Tethering Synthesis Strategy Toward High-Loading Atomically Dispersed Noble Metal Catalysts

Interfacial Coupling Between Noble Metal Nanoparticles and Metal-Organic Frameworks for Enhanced Catalytic Activity.

Interwrapping Distinct Metal-Organic Frameworks in Dual-MOFs for the Creation of Unique Composite Catalysts