Influence of K + on the crystal structure, defect, and scintillation performances of LYSO:Ce crystals
Peng Qiu,Zhongjun Xue,Chengyi Li,Aochen Zhang,Shuwen Zhao,Xiang Zheng,Zhe Zhang,Dongzhou Ding
DOI: https://doi.org/10.1016/j.jallcom.2024.174936
IF: 6.2
2024-05-31
Journal of Alloys and Compounds
Abstract:Lu 1.8 Y 0.2 SiO 5 :Ce (LYSO:Ce) crystals have become the material of choice for the current application of commercial TOF-PETs due to their high light output, short decay time, and fast rise time. In this study, a series of K + co-doped LYSO:Ce crystals were prepared by the μ-PD method, in which the K + concentrations were 0, 0.2 atom %, 0.6 atom %, and 1.0 atom %, respectively. It was found that the scintillation performances were simultaneously optimized when the K + concentration was 0.6 atom %. Compared to the sample of LYSO:Ce, LYSO:Ce, 0.6 atom % K showed an approximately 12.6 % increase in light yield, a shortening of the fastest scintillation decay time to 38.3 ns, and a 1.4-fold decrease in afterglow level. Moreover, the K + could replace the Lu 3+ site but could not cause the transition of Ce 3+ to Ce 4+ . Meanwhile, the connection between optical and luminescence performances and K + concentration was discussed. The luminescence contribution of Ce2 became stronger with the K + concentration increased. Furthermore, the research on K + co-doping of LYSO:Ce crystals could offer better knowledge and be informative for the selection of future co-dopants.
materials science, multidisciplinary,metallurgy & metallurgical engineering,chemistry, physical