Effect of aqueous solution and load on the formation of DLC transfer layer against Co-Cr-Mo for joint prosthesis.

Feifei Guo,Zhifeng Zhou,Meng Hua,Guangneng Dong

DOI: https://doi.org/10.1016/j.jmbbm.2015.04.014

IF: 4.042

2015-01-01

Journal of the Mechanical Behavior of Biomedical Materials

Abstract:Diamond-like carbon (DLC) coating exhibits excellent mechanical properties such as high hardness, low friction and wear, which offer a promising solution for the metal-on-metal hip joint implants. In the study, the hydrogen-free DLC coating with the element Cr as the interlay addition was deposited on the surface of the Co–Cr–Mo alloy by a unbalanced magnetron sputtering method. The coating thickness was controlled as 2µm. Nano-indentation test indicated the hardness was about 13GPa. DLC coated Co–Cr–Mo alloy disc against un-coated Co–Cr–Mo alloy pin (spherical end SR9.5) comprised the friction pairs in the pin-on-disc tribotest under bovine serum albumin solution (BSA) and physiological saline(PS).The tribological behavior under different BSA concetrations(2–20mg/ml), and applied load (2–15N) was investigated.DLC transfer layer did not form under BSA solution, even though different BSA concetration and applied load changed. The coefficient of friction(COF) under 6mg/ml BSA at 10N was the lowest as 0.10. A higher COF of 0.13 was obtained under 20mg/ml BSA. The boundary absorption layer of protein is the main factor for the counterparts. However, the continous DLC transfer layer was observed under PS solution, which make a lower COF of 0.08.