Abstract:Enhancing the energy storage capacity of carbon electrodes is a key challenge to developing high-performance supercapacitors. In this study, we design an oxygen-enriched hierarchical nanoporous carbon electrode using laser fabrication and subsequent electrochemical activation, which demonstrates superior energy storage capacity. The carbon electrode is first obtained through the carbonization of phenolic resin under instantaneous high temperature induced by laser, resulting in multiple ion transport channels and a specific capacitance of 64.17 mF cm–2 at the current density of 0.2 mA cm–2. To further improve the performance, electrochemical activation is successfully conducted, leading to a 12.1-fold increase of the specific capacitance of the carbon electrodes. It is found that O–CO-containing functional groups formed during the activation process significantly contribute to the high capacitance enhancement. In a 1 M H2SO4 electrolyte, the activated hierarchical nanoporous carbon electrode delivers a high specific capacitance of 778.3 mF cm–2 under the same test conditions. Additionally, the abundant porous structure and excellent reversibility of redox reaction of the oxygen-containing functional groups enable the assembled supercapacitor to obtain a specific capacitance of 45.3 mF cm–2 at the current density of 0.4 mA cm–2 and maintain a capacitance retention rate of 93.6% after 10,000 charge–discharge tests. This study presents a strategy to prepare carbon electrode materials with both high performance and excellent stability.

Oxygen-Rich Hierarchical Porous Carbon Derived from Artemia Cyst Shells with Superior Electrochemical Performance

Hydrangea-like N/O codoped porous carbons for high-energy supercapacitors

Sustainable Lignin-Derived Hierarchical Porous Carbon for Supercapacitors: A Novel Approach for Holding Electrochemical Attraction Natural Texture Property of Precursor

Nanoarchitectonics of fulvic acid based oxygen-rich hierarchical porous carbon with high specific surface area as supercapacitor electrodes

In-Situ Molten Salt Template Strategy For Hierarchical 3d Porous Carbon From Palm Shells As Advanced Electrochemical Supercapacitors

Multi-heteroatom-doped Hierarchical Porous Carbon Derived from Chestnut Shell with Superior Performance in Supercapacitors

Oxygen-Enriched Hierarchical Nanoporous Carbon Electrodes for Supercapacitors

Porous Carbon with Willow-Leaf-Shaped Pores for High-Performance Supercapacitors.

Hierarchically Porous Carbon Derived from an Aqueous Curable Composition for Supercapacitors

Mesoporous-rich and oxygen-rich hierarchical porous carbon derived from black humic acid for supercapacitor electrode

Hierarchical Porous Carbon Fabricated by NaCl-activated Artemisia Argyi Rod As Electrode Material for High-Performance Supercapacitor

Facile and low-cost fabrication of interconnected hierarchically porous carbon for high-performance supercapacitors

Preparation and Electrochemical Performance of Hierarchical Porous Carbons

Hierarchical Porous Carbon Aerogel Derived from Sodium Alginate for High Performance Electrochemical Capacitor Electrode

Hierarchical porous carbon sheets derived on a MgO template for high-performance supercapacitor applications

Oxygen Self-doped Hierarchical Porous Carbons Derived from Coal Liquefaction Residue for High-performance Supercapacitors in Organic and Ionic Liquid-based Electrolytes

Three-Dimensional Hierarchically Ordered Porous Carbons with Partially Graphitic Nanostructures for Electrochemical Capacitive Energy Storage

In-situ self-templating synthesis of 3D hierarchical porous carbons from oxygen-bridged porous organic polymers for high-performance supercapacitors

Facile Synthesis of Hierarchical Porous Carbon Nanorods for Supercapacitors Application

Hierarchically Porous Carbon by Activation of Shiitake Mushroom for Capacitive Energy Storage

High Capacitance Performance N, O Codoped Carbon Foams Synthesized via an All-In-One Step Carbonization of Molecular Salt Strategy