Abstract:This paper reports the synthesis of semiconductor nanocrystals of PbS through a facile and inexpensive synthetic route between lead acetate [Pb(Ac)2·3H2O] and dithioglycol (HSCH2CH2SH) without any surfactant. The products were characterized by x-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution TEM (HRTEM), Raman spectroscopy, x-ray photelectron spectroscopy (XPS) and infrared (IR) spectroscopy. The size of cube-shaped PbS nanocrystals can be controlled by changing the relative amount of Pb(Ac)2·3H2O and dithioglycol. Smaller cube-shaped PbS nanocrystals were obtained at higher sulfur content in the reaction system. The nanometre-sized single crystals of PbS measure ~83 nm × 59 nm × 22 nm and 39 nm × 10 nm × 7 nm, for lead acetate:dithioglycol ratios of 1:0.375 (denoted as PbS-1) and 1:1.5 (denoted as PbS-2), respectively, when a mixture of NaOH solution of lead acetate and ethyl alcohol solution of dithioglycol is maintained at 220 °C for 4 h in a Teflon-lined autoclave. XRD patterns and HRTEM images confirm the crystalline structure of the PbS crystals. TEM helped to determine the dimension of the single crystals. Raman, XPS and IR helped to further demonstrate the purity of the as-synthesized samples. The optical absorption spectra of suspensions of the these crystals in glycol show shifts in absorption band edge for as-prepared sample PbS-1 from 246 to 271 nm and for PbS-2 from 246 to 275 nm, after four days of storage, respectively. The photoluminescence peaks from the two samples are located at 434 and 433 nm for photoexcitation radiation of 315–355 nm, thus exhibiting a Stokes shift compared with band edge energy. The principal contribution of this work is that the nanometre-size PbS single crystals are prepared without using a surfactant or templating agent. The formation of a five-membered ring via the chelation between the Pb2+ ion and dithioglycol is considered to be crucial in this mechanism.

Sub-10 nm monodisperse PbS cubes by post-synthesis shape engineering.

Facile synthesis of PbS truncated octahedron crystals with high symmetry and their large-scale assembly into regular patterns by a simple solution route.

Shape Controllable Growth of PbS Polyhedral Crystals

Growth and photoluminescence properties of PbS nanocubes

Shape-Controlled Syntheses of Pbs Submicro-/Nano-Crystals Via Hydrothermal Method

PbS Cubes with Pyramidal Pits: An Example of Etching Growth

L-Cysteine-Assisted Synthesis of PbS Nanocube-Based Pagoda-like Hierarchical Architectures

High Yield Synthesis of PbS Nanocubes Using One-Step Solid-State Reaction in the Presence of an Anionic Surfactant

Surface Synthesis of PbS Nanoparticles on Silica Spheres by a Sonochemical Approach

Octahedron Shaped Lead Sulfide Nanocrystals As Counter Electrodes for Quantum Dot Sensitized Solar Cells

PbS Assemblies: the Oriented Attachment of Individual PbS Nanocrystals

Hierarchical, Star-Shaped Pbs Crystals Formed by A Simple Solution Route

Studies of synthesis and optical properties of ZnS nanocrystals

Growth of PbS crystals from nanocubes to eight-horn-shaped dendrites through a complex synthetic route

Formation of CsPbCl 3 Cubes and Edge-Truncated Cuboids at Room Temperature

Synthesis of PbS Nanorods and Other Ionic Nanocrystals of Complex Morphology by Sequential Cation Exchange Reactions

High yield synthesis of matchstick-like PbS nanocrystals using mesoporous organosilica as template

Shape controlled synthesis of PbS nanocrystals by a solvothermal–microemulsion approach

Cubic Form of Pb(2-x)Sn(x)S2 Stabilized Through Size Reduction to the Nanoscale.

Synthesis and the Growth Mechanism of PbS Nanorod

Controlled Synthesis, Growth Mechanism, and Properties of Monodisperse CdS Colloidal Spheres.