Abstract:Activities and selectivities of iron/palladium (Fe/Pd) bimetallic nanoparticles supported on various resin materials (chelating resins DOW 3N, cation-exchange resin D001, and anion-exchange resin D201) were studied for the reduction of nitrate in water. Scanning electron microscopy-energy dispersive spectrometry and transmission electron microscopy results indicated that the Fe/Pd bimetallic nanoparticles were well dispersed without aggregation on the three resin supports, indicating that the resins were favorable supports for Fe/Pd bimetallic nanoparticles. The surface chemistry of the support plays an important role in the activity and selectivity of Fe/Pd bimetallic nanoparticles. D201-Fe/Pd and DOW 3N-Fe/Pd exhibited high removal efficiency of nitrate (100% and 97.8%, respectively), whereas D001-Fe/Pd exhibited low efficiency (21.0%) of nitrate removal. This is mainly because the fixed negatively charged functional groups on the surface of D001 prevented nitrate permeation owing to the Donnan exclusion effect. Moreover, almost all reduction products with D001-Fe/Pd and D201-Fe/Pd were ammonia, whereas 69.2% N-2 selectivity was obtained with DOW 3N-Fe/Pd. The transfer of nitrite from the Fe surface to the Pd surface was regarded as a key step in determining the selectivity for N-2. There was no strong electrostatic repulsion or electrostatic attraction between nitrite and DOW 3N-Fe/Pd. The intermediate reduction product nitrite can be transformed from Fe to Pd freely, and can be reduced by H-ads on the surface of Pd to N-2, resulting in high N-2 selectivity. Therefore, the chelating resin, which has no strong electrostatic force between itself and nitrate, was suitable as the support for bimetallic nanoparticles to selectively reduce nitrate.

[Reductive Dechlorination of Atrazine by Ni/Fe Bimetallic Particles].

Rapid Treatment of Atrazine-Contaminated Water by Nickel/Iron Bimetallic System

The Dechlorination Degradation of Atrazine by Foam Nickel/iron Powder

Rapid Dechlorination of Chlorinated Organic Compounds by Nickel/iron Bimetallic System in Water

Catalytic Dechlorination of Aroclor 1242 by Ni/Fe Bimetallic Nanoparticles.

Electrocatalytic Dechlorination of Atrazine Using Binuclear Iron Phthalocyanine as Electrocatalysts

Mechanism and Influence Factors of 2,4‐D Dechlorination by Sodium Citrate‐activated Bimetallic Palladium‐zero Valent Iron Nanoparticles

Catalytic Dechlorination of P-Ncb in Water by Nanoscale Ni/Fe

Nitrate Reduction by Chelating Resin‐supported Fe and Fe/Ni Nanoparticles: Comparison of Reactivity and Effect of Co‐existing Inorganic Anion

Influence of nickel loading on reactivity of Ni/Fe bimetallic nanoparticles toward trichloroethene and carbon tetrachloride

Electrocatalytic Hydrodehalogenation of Atrazine in Aqueous Solution by Cu@Pd/Ti Catalyst.

Fast dechlorination of trichloroethylene by a bimetallic Fe(OH)2/Ni composite

Selective Reduction of Nitrate into Nitrogen Using Fe–Pd Bimetallic Nanoparticle Supported on Chelating Resin at Near-Neutral Ph

Experimental Identification of the Roles of Fe, Ni and Attapulgite in Nitroreduction and Dechlorination of p-Chloronitrobenzene by Attapulgite-Supported Fe/Ni Nanoparticles

Highly Active and Stable Ni-Fe Bimetal Prepared by Ball Milling for Catalytic Hydrodechlorination of 4-Chlorophenol

Removal of Ni~(2+) and catalytic dechlorination of chlorophenol from contaminated water by zero-valent iron

Dechlorination of Pentachlorophenol Using Nanoscale Fe/Ni Particles: Role of Nano-Ni and Its Size Effect

Fe–Pd Bimetallic Composites Supported by Resins for Nitrate Reduction: Role of Surface Functional Groups in Controlling Rate and Selectivity

Dechlorination of Excess Trichloroethene by Bimetallic and Sulfidated Nanoscale Zero-Valent Iron

Ruthenium decorated nickel-iron layered double hydroxides (NiFe-LDH) for promoting peroxymonosulfate activation and atrazine degradation

Synergistic Effect and Degradation Mechanism on Fe-Ni/CNTs for Removal of 2,4-Dichlorophenol in Aqueous Solution