Abstract:Attapulgite (ATP) disaggregated by a ball milling–freezing process was used to support Fe/Ni bimetallic nanoparticles (nFe/Ni) to obtain a composite material of D-ATP-nFe/Ni for the dechlorination degradation of 2,4-dichlorophenol (2,4-DCP), thus improving the problem of agglomeration and oxidation passivation of nanoscale zero-valent iron (nFe) in the dechlorination degradation of chlorinated organic compounds. The results show that Fe/Ni nanoparticle clusters were dispersed into single spherical particles by the ball milling–freezing-disaggregated attapulgite, in which the average particle size decreased from 423.94 nm to 54.51 nm, and the specific surface area of D-ATP-nFe /Ni (97.10 m2/g) was 6.9 times greater than that of nFe/Ni (14.15 m2/g). Therefore, the degradation rate of 2,4-DCP increased from 81.9% during ATP-nFe/Ni application to 96.8% during D-ATP-nFe/Ni application within 120 min, and the yield of phenol increased from 57.2% to 86.1%. Meanwhile, the reaction rate Kobs of the degradation of 2,4-DCP by D-ATP-nFe/Ni was 0.0277 min−1, which was higher than that of ATP-nFe/Ni (0.0135 min−1). In the dechlorination process of 2,4-DCP by D-ATP-nFe/Ni, the reaction rate for the direct dechlorination of 2,4-DCP of phenol (k5 = 0.0156 min−1) was much higher than that of 4-chlorophenol (4-CP, k2 = 0.0052 min−1) and 2-chlorophenol (2-CP, k1 = 0.0070 min−1), which suggests that the main dechlorination degradation pathway for the removal of 2,4-DCP by D-ATP-nFe/Ni was directly reduced to phenol by the removal of two chlorine atoms. In the secondary pathway, the removal of one chlorine atom from 2,4-DCP to generate 2-CP or 4-CP as intermediate was the rate controlling step. The final dechlorination product (phenol) was obtained when the dechlorination rate accelerated with the progress of the reaction. This study contributes to the broad topic of organic pollutant treatment by the application of clay minerals.

The Dechlorination Degradation of Atrazine by Foam Nickel/iron Powder

[Reductive Dechlorination of Atrazine by Ni/Fe Bimetallic Particles].

Rapid Treatment of Atrazine-Contaminated Water by Nickel/Iron Bimetallic System

Insights into Atrazine Degradation by Persulfate Activation Using Composite of Nanoscale Zero-Valent Iron and Graphene: Performances and Mechanisms

Rapid Dechlorination of Chlorinated Organic Compounds by Nickel/iron Bimetallic System in Water

A Novel Advanced Oxidation Process Using Iron Electrodes and Ozone in Atrazine Degradation: Performance and Mechanism

DEGRADATION OF ATRAZINE IN AQUEOUS SOLUTION BY GAS-LIQUID HYBRID DISCHARGE

Surface Fe(III)/Fe(II) Cycle Promoted the Degradation of Atrazine by Peroxymonosulfate Activation in the Presence of Hydroxylamine

Ruthenium decorated nickel-iron layered double hydroxides (NiFe-LDH) for promoting peroxymonosulfate activation and atrazine degradation

Application of a Novel Strategy—advanced Fenton-chemical Precipitation to the Treatment of Strong Stability Chelated Heavy Metal Containing Wastewater

Mechanism and Influence Factors of 2,4‐D Dechlorination by Sodium Citrate‐activated Bimetallic Palladium‐zero Valent Iron Nanoparticles

Removal of Ni~(2+) and catalytic dechlorination of chlorophenol from contaminated water by zero-valent iron

Degradation Of Atrazine (Atz) By Ammonia/Chlorine Synergistic Oxidation Process

Joint Degradation of Atrazine/Cationic Red X-GRL with Monophenolic Compound to Reduce Fe²+ Input in Fenton Process

Theoretical and experimental study on the degradation mechanism of atrazine in Fenton oxidation treatment

Dielectric Barrier Discharge Plasma Induced Degradation of Aqueous Atrazine.

Performance, Reaction Pathway and Kinetics of the Enhanced Dechlorination Degradation of 2,4-Dichlorophenol by Fe/Ni Nanoparticles Supported on Attapulgite Disaggregated by a Ball Milling–Freezing Process

Design of a multi-electrode dielectric barrier discharge reactor and experimental study on the degradation of atrazine in water

Removal Atrazine Using Two Anion-Exchange Resins Supported Nanohydrous Metal-Oxide Particle

Electrocatalytic Dechlorination of Atrazine Using Binuclear Iron Phthalocyanine as Electrocatalysts

Iron–doped bismuth oxybromides as visible−light−responsive Fenton catalysts for the degradation of atrazine in aqueous phases