Abstract:Attapulgite (ATP) disaggregated by a ball milling–freezing process was used to support Fe/Ni bimetallic nanoparticles (nFe/Ni) to obtain a composite material of D-ATP-nFe/Ni for the dechlorination degradation of 2,4-dichlorophenol (2,4-DCP), thus improving the problem of agglomeration and oxidation passivation of nanoscale zero-valent iron (nFe) in the dechlorination degradation of chlorinated organic compounds. The results show that Fe/Ni nanoparticle clusters were dispersed into single spherical particles by the ball milling–freezing-disaggregated attapulgite, in which the average particle size decreased from 423.94 nm to 54.51 nm, and the specific surface area of D-ATP-nFe /Ni (97.10 m2/g) was 6.9 times greater than that of nFe/Ni (14.15 m2/g). Therefore, the degradation rate of 2,4-DCP increased from 81.9% during ATP-nFe/Ni application to 96.8% during D-ATP-nFe/Ni application within 120 min, and the yield of phenol increased from 57.2% to 86.1%. Meanwhile, the reaction rate Kobs of the degradation of 2,4-DCP by D-ATP-nFe/Ni was 0.0277 min−1, which was higher than that of ATP-nFe/Ni (0.0135 min−1). In the dechlorination process of 2,4-DCP by D-ATP-nFe/Ni, the reaction rate for the direct dechlorination of 2,4-DCP of phenol (k5 = 0.0156 min−1) was much higher than that of 4-chlorophenol (4-CP, k2 = 0.0052 min−1) and 2-chlorophenol (2-CP, k1 = 0.0070 min−1), which suggests that the main dechlorination degradation pathway for the removal of 2,4-DCP by D-ATP-nFe/Ni was directly reduced to phenol by the removal of two chlorine atoms. In the secondary pathway, the removal of one chlorine atom from 2,4-DCP to generate 2-CP or 4-CP as intermediate was the rate controlling step. The final dechlorination product (phenol) was obtained when the dechlorination rate accelerated with the progress of the reaction. This study contributes to the broad topic of organic pollutant treatment by the application of clay minerals.

Synergistic Effect and Degradation Mechanism on Fe-Ni/CNTs for Removal of 2,4-Dichlorophenol in Aqueous Solution

Enhanced dechlorination of 2,4-dichlorophenol by recoverable Ni/Fe-Fe3O4 nanocomposites.

Preparation of Functionalized Pd/Fe-Fe3O4@MWCNTs Nanomaterials for Aqueous 2,4-Dichlorophenol Removal: Interactions, Influence Factors, and Kinetics.

Synergistic Elimination of Chlorophenols Using a Single-Atom Nickel with Single-Walled Carbon Nanotubes: The Roles of Adsorption, Hydrodechlorination, and the Electro-Fenton Process

Simultaneous Adsorption and Dechlorination of 2,4-Dichlorophenol by Pd/Fe Nanoparticles with Multi-Walled Carbon Nanotube Support

Mechanism and Influence Factors of 2,4‐D Dechlorination by Sodium Citrate‐activated Bimetallic Palladium‐zero Valent Iron Nanoparticles

Adsorption–dechlorination of 2,4-Dichlorophenol Using Two Specified MWCNTs-stabilized Pd/Fe Nanocomposites

Enhanced dechlorination of 2,4-dichlorophenol by Pd/FeFe3O4 nanocomposites

Biochar as an electron shuttle loaded with Fe/Ni bimetallic nanoparticles for efficient removal of 2,4-dichlorophenols: Performance, degradation pathway and mechanism

Catalytic Dechlorination of 2,4-Dichlorophenol in Water by Nanoscale Pd/Fe Bimetallic System

Dechlorination Mechanism of 2,4-Dichlorophenol by Ni/Fe Nanoparticles in the Presence of Humic Acid

Catalytic Dechlorination of P-Ncb in Water by Nanoscale Ni/Fe

Dechlorination of Pentachlorophenol Using Nanoscale Fe/Ni Particles: Role of Nano-Ni and Its Size Effect

Performance, Reaction Pathway and Kinetics of the Enhanced Dechlorination Degradation of 2,4-Dichlorophenol by Fe/Ni Nanoparticles Supported on Attapulgite Disaggregated by a Ball Milling–Freezing Process

Dechlorination Mechanism of 2,4-Dichlorophenol by Magnetic MWCNTs Supported Pd/Fe Nanohybrids: Rapid Adsorption, Gradual Dechlorination, and Desorption of Phenol

Dechlorination of 2,4-dichlorophenol by nanoscale magnetic Pd/Fe particles: Effects of pH, temperature, common dissolved ions and humic acid

Enhanced dechlorination of carbon tetrachloride by Ni-doped zero-valent iron nanoparticles @ magnetic Fe<sub>3</sub>O<sub>4</sub> (Ni<sub>4</sub>/Fe@Fe<sub>3</sub>O<sub>4</sub>) nanocomposites

Enhanced Electrocatalytic Cathodic Degradation of 2,4-Dichlorophenoxyacetic Acid Based on a Synergistic Effect Obtained from Co Single Atoms and Cu Nanoclusters

Atomically dispersed ternary FeCoNb active sites anchored on N-doped honeycomb-like mesoporous carbon for highly catalytic degradation of 4-nitrophenol

Efficient degradation of chlorinated phenolic compounds by Fe@Cu materials with enhanced oxygen reduction reaction

Influence of nickel loading on reactivity of Ni/Fe bimetallic nanoparticles toward trichloroethene and carbon tetrachloride