Abstract:Titania nanowire arrays have been deposited on Ti foils through direct oxidizing the Ti substrate with aqueous hydrogen peroxide solutions containing melamine and nitric acid, and the applicability of such nanowire arrays to back-illuminated dye-sensitized solar cells studied in parallel with titania nanotube arrays on Ti foils. The low-temperature nitrogen adsorption measurement reveals that the film with nanowires 25nm in diameter and 1μm in length possesses a BET specific surface area of 59.0m2g−1, a value much larger than 26m2g−1 calculated for the nanotube with an inner diameter of 80nm, an outer diameter of 120nm and a total length of 3μm. Assuming an indirect transition between band gaps, the nanowire film exhibits a bandgap of 3.1eV, slightly larger than that of 3.0eV for the nanotube one. A detailed electrochemical study suggests that, in comparison with the nanotube film, the nanowire one exhibits much lower saturated photocurrent and poorer conductivity under the Xe-lamp irradiation. However, when utilized to construct back-side illuminated dye-sensitized solar cells, the cell with the 2μm-thick nanowire photoanode possesses significantly higher efficiency than the one with the 3μm-thick nanotube photoanode. The relatively high energy conversion efficiency is contributed to the high specific surface area and the unique mesoporous structure of the titania nanowire arrays, which favors the adsorption of dye molecules.

Hydrothermal Fabrication of Hierarchically Anatase Tio2 Nanowire Arrays on Fto Glass for Dye-Sensitized Solar Cells

Hierarchical Submicroflowers Assembled from Ultrathin Anatase TiO2 Nanosheets As Light Scattering Centers in TiO2 Photoanodes for Dye-Sensitized Solar Cells

TiO2 Hierarchical Nanostructures: Hydrothermal Fabrication and Application in Dye-Sensitized Solar Cells

Fabrication of Morphology Controllable Rutile TiO2 Nanowire Arrays by Solvothermal Route for Dye-Sensitized Solar Cells

Facile Preparation of Hierarchical TiO2nanowire–nanoparticle/nanotube Architecture for Highly Efficient Dye-Sensitized Solar Cells

Rutile TiO2 nano-branched arrays on FTO for dye-sensitized solar cells.

Tio2 Nanowires/Zno Nanosheets Hierarchically Structure on Ti Foil As Flexible Photoanodes for Dye-Sensitized Solar Cells

A novel approach to titania nanowire arrays as photoanodes of back-illuminated dye-sensitized solar cells

Highly ordered hierarchical TiO2 nanotube arrays for flexible fiber-type dye-sensitized solar cells

Transparent, 3-Dimensional Light-Collected, And Flexible Fiber-Type Dye-Sensitized Solar Cells Based On Highly Ordered Hierarchical Anatase Tio2 Nanorod Arrays

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Fabrication of TiO 2 nanorod array/semiconductor nanocrystal hybrid structure for photovoltaic applications

Au/TiO2 Nanotube Array Based Multi-Hierarchical Architecture for Highly Efficient Dye-Sensitized Solar Cells

Hierarchical TiO2 microspheres comprised of anatase nanospindles for improved electron transport in dye-sensitized solar cells.

Ultralong Rutile TiO2 Nanowire Arrays for Highly Efficient Dye-Sensitized Solar Cells.

Ordered TiO2 Nanotube Arrays on Transparent Conductive Oxide for Dye-Sensitized Solar Cells

Dye-Sensitized Solar Cells with Vertically Aligned Tio2 Nanowire Arrays Grown on Carbon Fibers

Mesocrystalline Tio2 Nanosheet Arrays with Exposed {001} Facets: Synthesis Via Topotactic Transformation and Applications in Dye-Sensitized Solar Cells

Monodisperse Tio2 Hierarchical Hollow Spheres Assembled By Nanospindles For Dye-Sensitized Solar Cells

Growth of TiO2 Nanoflowers Photoanode for Dye-Sensitized Solar Cells