Abstract:The photoluminescence (PL) quantum yield (QY) of CdSe nanocrystals during their growth under a given set of initial conditions increases monotonically to a certain maximum value and then decreases gradually. Such a maximum is denoted as a PL "bright point", which does not always overlap with the minimum point of the PL peak width for the same reaction. The experimental results suggest that the existence of the PL bright point is a general phenomenon during the growth of semiconductor nanocrystals and likely is a signature of an optimal surface structure/reconstruction of the nanocrystals grown under a given set of initial conditions. The position of the bright point, the highest PL QY, the types of the bright points (sharp or flat), the sharpness of the PL peak, etc., were all strongly dependent on the initial Cd:Se ratio of the precursors in the solution. A large excess of the selenium precursor, with 5-10 times more selenium precursor than the amount of the cadmium precursor, was found necessary to achieve a high PL QY value and a narrow emission profile. The existence of the PL bright point and the sensitive temporal variation of the PL QY during the growth of semiconductor nanocrystals can explain the unpredictable nature and poor reproducibility of the PL properties of the as-prepared semiconductor nanocrystals observed previously. Furthermore, the knowledge gained in this study enabled us to reproducibly synthesize highly luminescent CdSe nanocrystals through a relatively simple and safe synthetic scheme. In a traditionally weak emission window for CdSe nanocrystals, the orange-red optical window, the PL QY of the as-prepared CdSe nanocrystals reached as high as 85% at room temperature, and the full width at half-maximum of the corresponding PL peak was as narrow as 23 nm, about 65-80 meV depending on the emitting position. The PL properties of the as-prepared CdSe nanocrystals are stable upon aging for at least several months. These as-prepared nanocrystals represent a series of best emitters that are highly efficient, highly pure in emission color, stable, and continuously tunable by simply varying the size of the nanocrystals.

Composition-Tunable Znxcd1-Xse Nanocrystals With High Luminescence And Stability

An Efficient Green-Emitting Quantum Dot with Near-Unity Quantum Yield and Suppressed Auger Recombination for High-Performance Light-Emitting Diodes

Large scale synthesis of stable tricolor Zn(1-x)Cd(x)Se core/multishell nanocrystals via a facile phosphine-free colloidal method.

Zn (ii)‐doped Cesium Copper Halide Nanocrystals with High Quantum Yield and Colloidal Stability for High‐Resolution X‑Ray Imaging

Control of Photoluminescence Properties of CdSe Nanocrystals in Growth.

Noninjection Synthesis of CdS and Alloyed CdS x Se 1−x Nanocrystals Without Nucleation Initiators

One-Temperature Synthesis of Doped and Alloyed Zn-Cd-Se Nanocrystals

Synthesis of Highly Luminescent Mercaptosuccinic Acid-Coated Cdse Nanocrystals under Atmospheric Conditions

Type-I CdSe@CdS@ZnS Heterostructured Nanocrystals with Long Fluorescence Lifetime

Synthesis of Colloidal Quantum Dots with an Ultranarrow Photoluminescence Peak

Luminescent AgGaSe2/ZnSe nanocrystals: rapid synthesis, color tunability, aqueous phase transfer, and bio-labeling application

Synthesis and Wavelength-Tunable Luminescence Property of Wurtzite Zn<sub><i>x</i></sub>Cd<sub>1−<i>x</i></sub>S Nanostructures

Alloyed (Znse)(x)(cuinse2)(1-X) and CuInSe(x)S(2-x) Nanocrystals with a Monophase Zinc Blende Structure over the Entire Composition Range.

Crystal Structure Control of Zinc-Blende CdSe/CdS Core/shell Nanocrystals: Synthesis and Structure-Dependent Optical Properties.

Optical Properties of Fully Inorganic, Spacer-Free Core/Gradient-Shell CdSe/CdZnS Nanocrystals at the Ensemble and Single-Nanocrystal Levels

Enhanced luminescence of ZnSe:Eu 3+/ZnS core-shell quantum dots

Cadmium-Alloyed Zinc Oxide Nanocrystals in the Quantum Confinement Region with Intense Visible Luminescence

Efficient and Color-Tunable Mn-Doped Znse Nanocrystal Emitters: Control of Optical Performance Via Greener Synthetic Chemistry

Synthesis and Pl Properties of Znse Nanowires with Zincblende and Wurtzite Structures

Emission Tuning of Highly Efficient Quaternary Ag-Cu-Ga-Se/ZnSe Quantum Dots for White Light-Emitting Diodes.

High Quality ZnSe and ZnS Nanocrystals Formed by Activating Zinc Carboxylate Precursors