Abstract:Understanding atomic-scale mechanisms of dislocation interacting with irradiation-induced nanosized voids is vital to predict in-service performances of nuclear components. In reality, multiple dislocations can sequentially interact with one void, namely, the already sheared void can be further sheared by incoming dislocations; however, previous work mostly focused on the first-time dislocation-void interaction and assumed that already sheared voids have the same hardening effects in subsequent interactions. Using atomistic simulations, this work studies the interaction mechanisms between a periodic array of voids and successively incoming edge dislocations, and corresponding hardening effects. Simulation results reveal that the sheared voids impede dislocation motion in the same manner as the unsheared ones do, but the resistance to dislocation glide could decrease with interaction times. As an edge dislocation is pinned by the void, a pair of screw dipole form on the dislocation. Then the screw arms move along the void surface through multiple-time cross-slip upon continuous shear deformation, until the dipole annihilate in or above the original slip plane at some critical stress, thereby releasing the dislocation. These atomic processes are also accompanied with absorbing vacancies from the void and climbing up of dislocation segment in each interaction event. Hardening effect of the sheared voids can be progressively weakened due to decreasing void size when interaction times exceeding some value. The hardening effects of sheared voids can be quantified by a modified Bacon-Kocks-Scttergood model, if adopting an effective diameter that is calculated from the major axis of the dislocation-void intersection region rather than the constant diameter of the unsheared void.

Atomistic Simulation of Voids Effect on Nanoindentation.

Atomic Simulation of Void Effect on the Microstructure Evolution and Internal Stress Transmission in Nanoindentation

Atomistic Investigations of Single-Crystal Silicon with Pre-Existing Defects

Atomistic Simulations of the Effect of a Void on Nanoindentation Response of Nickel

Quasicontinuum Simulation of Surface Step Effects on First Dislocation Emission in Nanoindentation

Atomistic modeling size dependence of nano-voided copper yielding under uniaxial tension

Dislocation nucleation in the initial stage during nanoindentation

Evolution of spherical nanovoids within copper polycrystals during plastic straining: Atomistic investigation

Nanoindentation Size Effect Interpreted by the Dislocation Nucleation Mechanism

Position Effect of Cylindrical Indenter on Nanoindentation into Cu Thin Film by Multiscale Analysis

Anisotropy in homogeneous dislocation nucleation by nanoindentation of single crystal Cu

Effects of Crystalline Anisotropy and Indenter Size on Nanoindentation by Multiscale Simulation.

Multiscale Simulation of Surface Step Effects on Nanoindentation

Multiscale Analysis of Delay Effect of Dislocation Nucleation with Surface Pit Defect in Nanoindentation

Atomistic Simulation of Twin Boundaries Effect on Nanoindentation of Ag(111) Films

Investigation on the Dislocation Evolution in Nanoindentation with 2.5D Discrete Dislocation Dynamics Simulation and Experiment

Atomistic Simulation of Deformation-Induced Crystallization Behavior During the Indentation Process for Amorphous Cu

Exploring the Effects of the Sheared Voids on the Hardening of Tungsten Using Atomistic Simulations

Effect of void morphology on void facilitated plasticity in irradiated Cu/Nb metallic nanolayered composites

Numerical and Experimental Studies of Deep Indentation on Single Crystals

Initial dislocation topologies of nanoindentation into copper (001) film with a nanocavity