Abstract:In the presence of surfactant, potassium stearate, quantum-confined InP nanocrystals (NCs) were hydrothermally synthesized in aqueous ammonia. Powder x-ray diffraction (XRD) patterns give the zinc blende phase of InP with lattice constant a=5.8377±8×10−4 Å. Transmission electron microscopy (TEM) micrographs show that the as-prepared InP NCs are spherical secondary particles (120 nm) consisting of spherical nanocrystals and rod-like nanocrystals grown in the direction perpendicular to the [111] direction, which is different from those grown by solution–liquid–solid process. X-ray photoelectron spectra indicate that the nanocrystals have a stoichiometric ratio of In:P=1.2:1 and their surfaces are capped with stearate ions. Powder XRD, TEM images, Raman spectra, optical absorption and photoluminescence spectra of InP NCs grown with surfactant were compared with those of the InP NCs grown without surfactant, and it indicated that the as-prepared InP NCs via surfactant-aided synthesis are quantum confined: their transverse optical and longitudinal optical vibration modes exhibit frequency redshifting and asymmetric broadening which is consistent with the phonon confinement model of nanoparticles. Compared with bulk values, InP NCs exhibit a band-edge emission band centered at 1.81 eV (685 nm) with a blueshift of 0.44 eV at 300 K. A wide distribution in size and the two-morphology nature of the NCs resulted in featureless absorption spectra and broadening of the emission band. The formation mechanism of the InP NCs is discussed and attributed to an in situ decomposition process of an indium polyphosphide amorphous precursor.

Aqueous synthesis of III-V semiconductor GaP and InP exhibiting pronounced quantum confinement.

Aqueous synthesis of III???V semiconductor GaP and InP exhibiting pronounced quantum confinementElectronic supplementary information (ESI) available: experimental details. See http://www.rsc.org/suppdata/cc/b2/b210164e/

A Developed Ullmann Reaction To Iii-V Semiconductor Nanocrystals In Sealed Vacuum Tubes

A novel method for the preparation of III-V semiconductors: sonochemical synthesis of InP nanocrystals.

Plasma etching of III-V semiconductors and mechanism of crystalline damage

Sol-gel Synthesis and Photoluminescence of InP Nanocrystals Embedded in Silica Glasses

Hydrothermal Preparation of Nanocrystalline Indium Phosphidein Non-Aqueous System

Colloidal Chemical Synthesis and Characterization of InAs Nanocrystal Quantum Dots

One-Pot Synthesis of Color-Tunable Narrow-Bandwidth Ag-In-Ga-Zn-S Semiconductor Nanocrystals for Quantum-Dot Light-Emitting Diodes

Aqueous‐Solution Growth of GaP and InP Nanowires: A General Route to Phosphide, Oxide, Sulfide and Tungstate Nanowires.

Synthesis and Characterization of Indium Phosphide Nanocrystallite

Formation of Size-Tunable and Nearly Monodisperse InP Nanocrystals: Chemical Reactions and Controlled Synthesis

General Synthesis of I-III-VI2 Ternary Semiconductor Nanocrystals.

One-pot synthesis of Ag-In-Ga-S nanocrystals embedded in a Ga2O3 matrix and enhancement of band-edge emission by Na+ doping

Colloidal InP nanocrystals as efficient emitters covering blue to near-infrared.

Synthesis and Phase Transformation of In2se3 and Cuinse2 Nanowires

Vapor–liquid–solid growth of highly stoichiometric gallium phosphide nanowires on silicon: restoration of chemical balance, congruent sublimation and maximization of band-edge emission

Recent advances in the liquid synthesis of group Ⅳ-Ⅵ semiconductor nanocrystals

Inp Nanocrystals Via Surfactant-Aided Hydrothermal Synthesis

InP Quantum Dots: Synthesis and Lighting Applications.

InP Semiconductor Nanocrystals: Synthesis, Optical Properties, and Applications