Abstract:The Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers were prepared using sol-gel process combined with electrospinning. The thermal decomposition and phase inversion process of precursor nanofibers and the effects of calcination temperature and SiO2 content on the phase composition, microstructure, morphology and magnetic property of the resulting nanofibers were studied by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, high resolution transmission electron microscopy and vibrating sample magnetometer. The experimental results show that the cubic spinel structure is basically formed when the precursor nanofibers are calcined at 450 ℃ for 2 h. The average grain size of Ni0.5Zn0.5Fe2O4 contained in the composite nanofibers with 10 % SiO2 and their specific saturation magnetization and coercivity increase with increasing calcination temperature. Amorphous SiO2 additive can effectively restrain the growth of Ni0.5Zn0.5Fe2O4 nanocrystals. As a result, with SiO2 content increasing from 0 to 20 % , the average grain size of Ni0.5Zn0.5Fe2O4 in the prepared Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers calcined at 900 ℃ for 2 h decreases from 81.6 to 13.3 nm, and the specific saturation magnetization of these samples monotonically decreases, whereas the coercivity initially increases and then decreases due to the change of magnetic domain structure from multi-domain to single-domain along with the reduction in grain size. In addition, with the increase of SiO2 content, the diameter of the as-prepared Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers gradually increases and the surface becomes smooth.

Facile Synthesis of Superparamagnetic Ni-Fe Ultrafine Nanoalloy Nanoparticles with Equilibrium Ordered Phase Structure Via A Sol-Gel Process

Synthesis of iron–nickel nanoparticles via a nonaqueous organometallic route

A Novel Sol–gel Process to Facilely Synthesize Ni3Fe Nanoalloy Nanoparticles Supported with Carbon and Silica

Sol-gel preparation and characterization of NiCo and Ni3Fe nanoalloys

The Facile Synthesis, Crystallization Behavior and Magnetic Property of FeNiP Amorphous Nanoparticles

Chemical Synthesis of Monodisperse Fe-Ni Nanoparticles Via A Diffusion-Based Approach

Size-controlled synthesis and magnetic properties of NiFe2O4 hollow nanospheres via a gel-assistant hydrothermal route

Facile synthesis of nickel nanoparticles supported on carbon and silica matrix via a novel silica sol–gel process

Synthesis and Magnetic Properties of Fe–Ni Alloy Nanoparticles Obtained by Hydrothermal Reaction

Preparation of One-Dimensional Ni0.5 Zn0.5 Fe2O4/SiO2 Composite Nanostructures and Their Magnetic Properties

Structure and Magnetic Properties of Nife2o4 Nanoparticles Prepared by Low-Temperature Solid-State Reaction

Synthesis and Self-Assembly of Nickel-Substituted Ferrite Nanoparticles with Controlled Morphology and Chemical Composition

Nanostructural and Magnetic Studies of Virtually Monodispersed NiFe2O4 Nanocrystals Synthesized by a Liquid–solid-Solution Assisted Hydrothermal Route

Preparation and Characterization of Iron-Nickel Alloy Nanoparticles

Magnetic Properties of Ni Ferrite Nanocrystals Dispersed in the Silica Matrix by Sol–gel Technique

Synthesis and Magnetic Studies of Fe–Ni Nanofibres by Electrospinning

Solid State Synthesis of NiFe_2O_4 Nanoparticles at Low Temperature

Controlled Synthesis of Magnetic Spinel-Type Nickel Ferrite Nanoparticles by the Interface Reaction and Hydrothermal Crystallization

Preparation and Characterization of Wire-Liked NiFe2O4 Nanoparticles with High Specific Area and Excellent Magnetic Properties Via a Template-Assembled Sol-Gel Method

Microstructure and Magnetic Properties of Fe(x)Ni(1-x) Alloy Nanoplatelets.

Low-Temperature Synthesis of Superparamagnetic Nanocomposite Particles Composed of Platinum and Maghemite