Abstract:The content and depolymerization degree of the glass phase in coal fly ash (CFA) is positively correlated with the activity of CFA, which is one of the key factors in the comprehensive utilization of this ash. At present, the most common and accurate method for quantitative analysis of fly ash is selective dissolution. However, more experimental data are needed to specify the effect of HF concentration on reaction kinetics, the dissolution rate of amorphous phases, and the formation of new amorphous and crystalline phases. In this study, the effects of reaction temperature, reaction time, and hydrofluoric acid concentration on the leaching rate of CFA were investigated with a single-factor condition experiment and orthogonal experiment. Phase composition and transformation of CFA under different conditions were observed with XRD and SEM. The results show that with increasing reaction time (5–120 min), temperature (20–80°C), and HF concentration (5% to 30%), the leaching rate of CFA also increased from 29.4% to 90.2%. The phase transformation of CFA in acid solution is as follows: in 5% hydrofluoric acid concentration solution, the original glass phase disappears totally and a new glass phase is formed; in 15% hydrofluoric acid concentration solution, quartz disappears and a new phase named ralstonite [Na 0.5 Mg 0.5 Al 1.5 F 4 (OH) 2 · (H 2 O)] is formed; and when the hydrofluoric acid concentration reaches 30%, mullite disappears and a new phase named potassium aluminum fluoride (KAlF 4 ) is formed. Also, when the temperature rises to 80°C, the f-CaO in CFA participates in the reaction to form creedite (Ca 3 Al 2 SO 4 F 7.5 (OH) 2.5 · 2H 2 O) and fluorite (CaF 2 ). Reaction kinetics demonstrate that the leaching reaction to the glass body of CFA is a diffusion-controlled process, and the apparent activation energy of the Si and Al leaching reaction in glass phase is 11.62 kJ/mol and 26.039 kJ/mol, respectively.

Stability of CaF2 at High Temperature

Fluidization of Cohesive Fluorite Particles at Ambient/High Temperatures and Enhancement Methods

STUDY ON STABILITY OF CaCl2 AT HIGH TEMPERATURE

Impact of Fluorine on the Thermal Stability of Phlogopite

Molecular Dynamics Simulations for Melting Temperatures of Caf2

Study on Fluoride Emission from Soils at High Temperature Related to Brick-Making Process

High-temperature Relaxations in CaF2 Single Crystals

Pressure-induced structural transition in CaF2 nanocrystals

Temperature Dependences of Hydrous Species in Feldspars

Kinetics and phase transformation of low-calcium coal fly ash (CFA) under hydrofluoric acid leaching

Structural Stability of Hafnia-Based Materials at Ultra-High Temperature

First-Principles Study Of Structural Stabilities, And Electronic And Optical Properties Of Caf2 Under High Pressure

Fluorine Removal Efficiency of Organic-Calcium During Coal Combustion

High-temperature behaviour of fluorcarletonite, KNa4Ca4Si8O18(CO3)4(F,OH)⋅H2O, from the Murun Alkaline Complex, Russia, appraised by experimental and theoretical methods

Thermodynamic Stability and Dissolution of Calcium Fluoride of Phosphogypsum Solidified in Cement-Based Cementing Materials in Bicarbonate Solution

Effect of CaF2 on sintering behavior and thermal shock resistance of Y2O3 materials

The Study Of Decomposition Of Calcium Sulfate With Compound Molecule At High Temperature

Effect of CaF2 on the Electrical Properties of Yttria-Stabilized Zirconia

EXPERIMENTAL STUDY ON FLUORINE RETENTION PROCESS AND ADDITIVE UNDER HIGH TEMPERATION DURING COAL COMBUSTION

Factors Influencing The Stability Of Afm And Aft In The Ca-Al-S-O-H System At 25 Degrees C

Experimental Phase Equilibria Studies in the FeO-Fe2O3-CaO-Al2O3 System in Air