Abstract:This study aimed to enhance the sinterability and conductivity of yttria fully stabilized zirconia electrolyte through co-doping by 2 mol% of ZnO and different contents of MnO 2 (0, 0.5, 1, 1.5 mol%) at two sintering temperatures of 1300 and 1400 °C. Phase composition identification, density, microstructure, and conductivity of the samples were evaluated using X-ray diffraction (XRD), Archimedes' method, field emission scanning electron microscopy (FESEM), and electrochemical impedance spectroscopy (EIS), respectively. The XRD results revealed that ZnO and MnO 2 are successfully doped in the fluorite structure of YSZ sintered at 1400 °C, and the cubic structure is completely preserved. However, at a sintering temperature of 1300 °C, the (111) peaks of doped samples were slightly split, which implied a slight phase transformation of YSZ from cubic to a tetragonal structure. The co-doped samples, at both sintering temperatures, showed higher relative density and grain size compared with pure YSZ. The addition of 2 mol% of ZnO and 0.5 mol% of MnO 2 at 1400 °C increased the relative density of YSZ from 81.6% to 95.1%. The increase in relative density and grain size, while maintaining the cubic structure, caused an increase in the conductivity of the mentioned sample. Compared with pure YSZ, the sample's total conductivity increased from 7.37 to 10.03 S m −1 at 800 °C. The proposed composition showed better sintering behavior, lower activation energy of grain conductivity, and higher conductivity than pure YSZ. This behavior is thought to be due to the facilitating rearrangement of atoms during sintering and an increase in oxygen ion vacancy concentration due to co-doping with the appropriate amount of ZnO and MnO 2 .

Effect of CaF2 on the Electrical Properties of Yttria-Stabilized Zirconia

Cubic Yttria Stabilized Zirconia Sintering Additive Impacts: A Comparative Study

Effect of CaF2 on sintering behavior and thermal shock resistance of Y2O3 materials

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Enhancement of the ionic conductivity of mixed calcia/yttria stabilized zirconia

Effect of Li2o Additions Upon the Crystal Structure, Sinterability and Electrical Properties of Yttria Stabilized Zirconia Electrolyte

Microstructures and mechanical properties of 8Y-FSZ ceramics with BaTiO3 additive

Effect Of Bismuth Oxide On The Microstructure And Electrical Conductivity Of Yttria Stabilized Zirconia

Effects of CaF2 Additions on the Dielectric and Tunable Properties of Barium Strontium Titanate Ceramics

Effects of CaF2 on the sintering and crystallisation of CaO–MgO–Al2O3–SiO2 glass-ceramics

Effects of CaF2 Addition on the Microstructure and Microwave Dielectric Properties of ZnNb2O6 Ceramics

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics

Enhancing sintering behavior and conductivity of YSZ electrolyte by co-doping of ZnO and MnO 2

Microwave dielectric properties of CaF2-doped ZnNb2O6 ceramics

Temperature-dependence of the lattice conductivity of mixed calcia/yttria-stabilized zirconia

EFFECT OF DOPING CaO ON DIELECTRIC PROPERTIES OF BaZr0.05Ti0.95O3 CERAMICS

Fabrication and Characterization of La0.6Sr0.4Co0.2Fe0.8O3-δ-Yttria Stabilized Zirconia Composites Cathode Prepared by Infiltration Method

Influence of Doped YF3 on the Dielectric Properties of Barium Strontium Titanate Ceramics

Effects of Lithium Fluoride Additives on the Microstructure and Dielectric Properties of Barium Strontium Titanate Ceramics

Effect of Ca dopant on magnetic and magnetodielectric properties of Y3Fe5O12

Critical evaluations on the crystallographic properties of translucent dental zirconia ceramics stabilized with 3-6 mol% yttria