Abstract:We demonstrate the fabrication of sub-20 nm gate-all-around silicon (Si) nanowire field effect transistor structures using self-assembly. To create nanopatterned Si feature arrays, a block-copolymer-assisted hard mask approach was utilized using a topographically patterned substrate with well-defined Si3N4 features for graphoepitaxially alignment of the self-assembled patterns. Microphase-separated long-range ordered polystyrene-b-poly(ethylene oxide) (PS-b-PEO) block-copolymer-derived dot and line nanopatterns were achieved by a thermo-solvent approach within the substrate topographically defined channels of various widths and lengths. Solvent annealing parameters (temperature, annealing time, etc.) were varied to achieve the desired patterns. The BCP structures were modified by anhydrous ethanol to facilitate insertion of iron oxide features within the graphoepitaxial trenches that maintained the parent BCP arrangements. Vertical and horizontal ordered Si nanowire structures within trenches were fabricated using the iron oxide features as hard masks in an inductively coupled plasma (ICP) etch process. Cross-sectional micrographs depict wires of persistent width and flat sidewalls indicating the effectiveness of the mask. The aspect ratios could be varied by varying etch times. The sharp boundaries between the transistor components was also examined through the elemental mapping.This article has not yet been cited by other publications.

Epitaxial Graphene Nanoribbon Array Fabrication Using BCP-assisted Nanolithography.

Boundary-Directed Epitaxy of Block Copolymers

Fabrication of Graphoepitaxial Gate-All-Around Si Circuitry Patterned Nanowire Arrays Using Block Copolymer Assisted Hard Mask Approach

Large-Scale Production Of Graphene Nanoribbons From Electrospun Polymers

OWL-based Nanomasks for Preparing Graphene Ribbons with Sub-10 Nm Gaps.

Rational Fabrication of Graphene Nanoribbons Using a Nanowire Etch Mask

Densely aligned graphene nanoribbons at ∼35 nm pitch

Ultralong, High Aspect Ratio Graphene Nanoribbon Arrays Fabricated by Laser Interference Lithography: Implications for Integrated Nanocircuits

A Large-Area 15 Nm Graphene Nanoribbon Array Patterned by a Focused Ion Beam.

Directed self-organization of graphene nanoribbons on SiC

Substrate Engineering-Tailored Fabrication of Aligned Graphene Nanoribbon Arrays: Implications for Graphene Electronic Devices

Graphene edge lithography.

Fabrication of Graphene Nanodisk Arrays Using Nanosphere Lithography

Direct Fabrication of Well-Aligned Free-Standing Mesoporous Carbon Nanofiber Arrays on Silicon Substrates

Direct Growth of Graphene Nanoribbons for Large-Scale Device Fabrication

Narrow Graphene Nanoribbons from Carbon Nanotubes

Rapid Fabrication of Designable Large‐Scale Aligned Graphene Nanoribbons by Electro‐hydrodynamic Nanowire Lithography

Synthesis of Graphene Nanoribbons by Ambient-Pressure Chemical Vapor Deposition and Device Integration

Width-tunable Graphene Nanoribbons on a SiC Substrate with a Controlled Step Height.

Graphene Nanoribbon Superlattices Fabricated Via He Ion Lithography

In situ growth of large-area and self-aligned graphene nanoribbon arrays on liquid metal