Abstract:BaTi 2 O 5 (BT2) nanowires were successfully prepared via molten-salt method. The effects of synthesized temperature, dwell time, and molten salt concentration on the formation of BT2 nanowires were studied. X-ray diffraction patterns reveal that the BT2 nanowires crystallize in a monoclinic crystal structure. Neither the longer dwell time nor molten salt concentration has apparent influence on the formation of BT2 phase structure, whereas the synthesized temperature exerts great effect on the morphology of BT2 nanowires. One-dimensional morphology of the BT2 products was only obtained at a narrow temperature window (870–900 °C). At 970 °C, the morphology of BT2 nanowires was destroyed and they are broken into particles, growing as large flat crystals. The BT2 nanowires synthesized at 900 °C exhibit uniform morphology and grow in the [010] direction, which have an average diameter of 780 nm and length of 15 μm. The formation mechanism of BT2 nanowires in the MSS process is proposed. The BT2 nanowires exhibit the single-crystalline characteristics, as proven by high-resolution TEM images and electron diffraction patterns. Quantitative X-ray energy-dispersive spectroscopy analysis shows the BT2 nanowires having homogeneous chemical compositions, and their atomic cation ratio of Ba:Ti is 1:2.16. Dielectric properties of the BT2 nanowires synthesized at 900 °C are measured at room temperature with the frequency ranged from 10 2 to 10 6 Hz. The BT2 nanowires exhibit almost frequency independent dielectric behavior with dielectric constants of 28–31. The dielectric losses remain constant value of ~ 0.02 below 10 5 Hz, and increase up to 0.04 at 10 6 Hz.

Thermal conductivity and secondary porosity of single anatase TiO₂ nanowire.

Transient Thermal Characterization of Single Anatase TiO 2 nanowire with secondary porous structure

Thermo-physical Properties of Thin Films Composed of Anatase TiO2 Nanofibers

Effect of Annealing Temperature on Wettability of TiO2 Nanotube Array Films.

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Nonlinear Effects In Transient Electrothermal Characterization Of Anatase Tio2 Nanowires

Anisotropic Thermal Transport in Highly Ordered TiO2 Nanotube Arrays

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Preparation and Characterization of Anatase TiO2 Nanowires Using Hydrothermal Synthesis Method

Thermal Transport of Tin Dioxide Nanowires

Thermal Conductivity of Nanoporous Gold Microwires at Different Annealing Temperatures

Dielectric and Ferroelectric Properties of BaTiO3 Nanofibers Prepared Via Electrospinning

Microstructural Characterization and Dielectric Properties of Single Crystalline BaTi2O5 Nanowires Prepared by Molten-Salt Method

From nanorods to atomically thin wires of anatase TiO(2): nonhydrolytic synthesis and characterization.

Mesoporous TiO2-B nanowires synthesized from tetrabutyl titanate

Crystalline phase transformation of electrospinning TiO2 nanofibres carried out by high temperature annealing

Mechanical and Electronic Properties of TiO_2 Nanotubes

Synthesis of Anatase TiO2 Nanowires by Modifying TiO2 Nanoparticles Using the Microwave Heating Method

Thermal Characterization of Micro/nanoscale Conductive and Non-Conductive Wires Based on Optical Heating and Electrical Thermal Sensing

Electrical Transport Properties of Polycrystalline and Amorphous TiO2 Single Nanotubes

Porous TiO2 Nanowires Derived from Nanotubes: Synthesis, Characterzation and Their Enhanced Photocatalytic Properties