Abstract:Owing to their unique structural advantages, TiO2 hierarchical nanostructures assembled by low-dimensional (LD) building blocks have been extensively used in the energy-storage/-conversion field. However, it is still a big challenge to produce such advanced structures by current synthetic techniques because of the harsh conditions needed to generate primary LD subunits. Herein, a novel one-dimensional (1D) TiO2 hierarchical porous fibrous nanostructure constructed by TiO2 nanobelts is synthesized by combining a room-temperature aqueous solution growth mechanism with the electrospinning technology. The nanobelt-constructed 1D hierarchical nanoarchitecture is evolves directly from the amorphous TiO2/SiO2 composite fibers in alkaline solutions at ambient conditions without any catalyst and other reactant. Benefiting from the unique structural features such as 1D nanoscale building blocks, large surface area, and numerous interconnected pores, as well as mixed phase anatase-TiO2(B), the optimum 1D TiO2 hierarchical porous nanostructure shows a remarkable high-rate performance when tested as an anode material for lithium-ion batteries (107 mA h g-1 at ∼10 A g-1) and can be used in a hybrid lithium-ion supercapacitor with very stable lithium-storage performance (a capacity retention of ∼80% after 3000 cycles at 2 A g-1). The current work presents a scalable and cost-effective method for the synthesis of advanced TiO2 hierarchical materials for high-power and stable energy-storage/-conversion devices.

Asymmetric Anatase TiO2 Nanocrystals with Exposed High-Index Facets and Their Excellent Lithium Storage Properties

Crystalline SnO2 @ Amorphous TiO2 Core-Shell Nanostructures for High-Performance Lithium Ion Batteries

Nanoporous Anatase TiO2 Mesocrystals: Additive-Free Synthesis, Remarkable Crystalline-Phase Stability, and Improved Lithium Insertion Behavior.

Rational synthesis and lithium storage properties of hierarchical nanoporous TiO2(B) assemblies with tailored crystallites and architectures

Synthesis of Anatase Tio2 Nanocrystals with Exposed {001} Facets

One-pot synthesis of N-F-Cr-doped anatase TiO₂ microspheres with nearly all-(001) surface for enhanced solar absorption.

Size-Tunable Single-Crystalline Anatase TiO2 Cubes As Anode Materials for Lithium Ion Batteries

Architectural Design and Phase Engineering of N/B-Codoped Tio2(B)/Anatase Nanotube Assemblies for High-Rate and Long-Life Lithium Storage

Mesoporous TiO2 Single-Crystal Polyhedron-Constructed Core–Shell Microspheres: Anisotropic Etching and Photovoltaic Property

Tetragonal Faceted-Nanorods of Anatase TiO2 Single Crystals with a Large Percentage of Active {100} Facets.

Mesocrystalline Tio2 Nanosheet Arrays with Exposed {001} Facets: Synthesis Via Topotactic Transformation and Applications in Dye-Sensitized Solar Cells

Surface-reconstructed Formation of Hierarchical TiO2 Mesoporous Nanosheets with Fast Lithium-Storage Capability

3D anatase TiO2 hollow microspheres assembled with high-energy {001} facets for lithium-ion batteries

Hierarchical rutile TiO2 microspheres assembled by nanorods with nanocavities and their lithium-ion storage properties

Shape‐ and Size‐Controlled Synthesis of Uniform Anatase TiO2 Nanocuboids Enclosed by Active {100} and {001} Facets

Controllable Synthesis of Tio2 Single Crystals with Tunable Shapes Using Ammonium-Exchanged Titanate Nanowires As Precursors

Surface-reconstructed formation of hierarchical TiO<sub>2</sub> mesoporous nanosheets with fast lithium-storage capability

Self-Reconstructed Formation of a One-Dimensional Hierarchical Porous Nanostructure Assembled by Ultrathin TiO2 Nanobelts for Fast and Stable Lithium Storage.

Surface-reconstructed formation of hierarchical TiO 2 mesoporous nanosheets with fast lithium-storage capability

TiO2 Hollow Spheres Composed of Highly Crystalline Nanocrystals Exhibit Superior Lithium Storage Properties.

Hollow Nanocubes Constructed from <001> Oriented Anatase TiO2nanoarrays: Topotactic Conversion and Fast Lithium-Ion Storage