Abstract:In this paper, perfect interface model of Al/AlCu alloy and defect interface model of Al/AlCu alloy after cracks were introduced at different positions of the interface were established by using cohesive zone modeling method. Classical molecular dynamics simulation was used to study the deformation behavior and microstructure evolution of Al/AlCu alloy interface model at a strain rate of 0.05 Å/ps and the temperature of 300 K. The simulation results show that perfect interface exhibits a uniform plastic deformation stage due to structural relaxation after yielding, while there is no structural relaxation during the deformation of defect interface and the tensile strength is much lower than that of perfect interface as well. In the process of deformation, stacking faults formed in perfect interface and cracks are generated and expanded in Al matrix, while there was no stacking faults forming along with the expansion and cracking at the position of introduced cracks in defect interface. Massive dislocation nucleation leads to the reduction in stress at the perfect and defect interfaces after yielding. The extension of Shockley partial dislocation and the nucleation of Stair-rod dislocation are the main mechanisms of interface deformation. Densities of Shockley partial dislocation and Stair-rod dislocation decrease with increasing strain before crack propagation. This study enriches the analysis of microstructure evolution of Al/AlCu alloy interface and similar interfaces during deformation.

Theoretical Study of (ag,au and Cu)/Al2O3 Interfaces

Interface reconstruction and dislocation networks for a metal/alumina interface: an atomistic approach

The Interaction Between Misfit Dislocations at the Metal/Mgo Interfaces: Atomistic Study and Analysis

Atomistic Simulation of Misfit Dislocation in Metal/oxide Interfaces

Mechanical behavior and microstructure evolution of Al/AlCu alloy interface

Theoretical Study of Misfit Dislocation in Interface Dynamics

An Atomistic Simulation and Phenomenological Approach of Misfit Dislocation in Metal/Oxide Interfaces

Atomistic Study of Misfit Dislocation in Metal/sic(111) Interfaces

Tensile Properties and Fracture Mechanism of the Ti2AlC(0001)/TiAl(111) Interface: Insights from a First-Principles Study

Characterization and energy calculation of the S/Al interface of Al–Cu–Mg alloys: Experimental and first-principles calculations

The peculiarity of the metal-ceramic interface

Molecular dynamics simulations of interface structure and deformation mechanisms in metal/ceramic composites under tension

A Generalized O-element Approach for Analyzing Interface Structures

First-principles calculations of (0 0 1)α-Al//(0 0 1)θ' interface in Al-Cu alloys: Atomic structure, bonding strength, stability and electronic properties

Investigating interfacial segregation of Ω /Al in Al-Cu alloys: A comprehensive study using density functional theory and machine learning

Friction, Slip and Structural Inhomogeneity of the Buried Interface

Interaction of Dislocations and Interfaces in Crystalline Heterostructures: A Review of Atomistic Studies

Interfacial Potential Approach for Ag/Zno (0001) Interfaces

The Stability and Electronic Structure of Cu(200)/AuCu(200) Interface: An Insight from First-Principle Calculation

Influence of Defects During the Tensile Deformation of Cu–Al Joint Interfaces at the Nano Scale

Characterization and theoretical calculations of the T( Al 20 Cu 2 Mn 3 )/Al interface in 2024 alloys: TEM and DFT studies