Raman Spectroscopy Studies on the Structure of Moo3/Zro2 Solid Superacid
BY Zhao,XY Wang,HR Ma,YQ Tang
DOI: https://doi.org/10.1016/1381-1169(96)00008-8
1996-01-01
Abstract:MoO3ZrO2 prepared by different methods are distinctive in catalytic behavior. MoO3ZrO2 (MZ) obtained by impregnating crystallized ZrO2 and then calcining at high temperature is a catalyst for partial oxidation. However, MoO3ZrO2 (MZH) obtained by impregnating Zr(OH)4 and then calcining at high temperature is a solid superacid. It has been proved by Raman spectroscopy that they have different structural characteristics. In the MZ sample MoO3 is present as a monolayer, i.e., two-dimensional polymolybdates on monoclinic ZrO2, whose characteristic broad band is at about 950 cm−1. As MoO3 content is beyond its monolayer dispersion capacity (0.12 g MoO3100 m2 ZrO2), the surplus MoO3 is present as crystalline MoO3, whose intense peaks are at 820 and 994 cm−1. As for MZH sample, MoO3 exists on metastable tetragonal ZrO2 (ZrO2(t)) in two kinds of surface states, i.e., two-dimensional polymolybdates and MoOZr surface species which have a broad band at about 814 cm−1. Mo(VI) in MoOZr surface species is tetra-coordinated and bonds strongly with ZrO2(t). As MoO3 content in MZH sample exceeds a certain value, bulk Zr(MoO4)2 appears, which is indicated by the appearance of sharp peaks at 750, 946, 326 and 1002 cm−1. Quantitative Raman measurements for the three states of MoO3 in MZH samples show that the MoOZr surface species may be a preliminary compound of bulk Zr(MoO4)2. There is a good corresponding relation between its content and the catalytic activity of the superacid, therefore it should be responsible for its superacidity.