Preparation and characterization of Cu(I)/SO42-/ZnO and Cu(I)/S2O82-/ZnO catalysts
Li Zhong,Hai-Bin Huang,Xie Ke-Chang
2008-01-01
Abstract:Two novel solid acids of SO42-/ZnO and S2O82-/ZnO were prepared by impregnating H2SO4, (NH4)(2)S2O8 solution respectively on amorphous zinc oxide and calcining at 500-600 degrees C, and then used as carriers to prepare Cu(I)/SO42-/ZnO and Cu(I)/S2O82-/ZnO catalysts via solid-state ion-exchange. The solid acids and catalysts were characterized by XRD, FTIR, TPD and TPR. It is observed that Zn3O(SO4)(2) was formed during the preparation of the solid acids, and both of Lewis and Bronsted acid sites were formed on SO42-/ZnO and S2O82-/ZnO. NH3-TPD shows that both SO42-/ZnO and S2O82-/ZnO were very strong solid acids because the temperature of NH3 desorption peaks were above 543 degrees C. It is suggested by molecule structure analysis that the form of acid sites is due to the strongly electronic inductive effect of SO42-, the bridge-coordination complex of ZnO and SO42- causes the formation of Bronsted and Lewis acid sites on the surface, but the chelate-coordination complex of ZnO and SO42- has not any contribution to acid sites. Prepared by solid-state ion-exchange with the solid acids and CuCl at high temperature in N-2 follow, Cu(I)/SO42-/ZnO and Cu(I)/S2O82-/ZnO catalysts, in which Cu(I) was easy to reduced, showed an excellent catalytic behavior in the oxidative carbonylation of methanol to dimethyl carbonate (DMC). Both of the catalysts showed high catalytic acitivity and selectivity: 97.13% selectivity of DMC based on methanol and 1.87 g/(g.h) space-time yield, respectively.