Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Effect of Temperature on the Morphology of Silver Nanoparticles on Si Substrate in the Silver Mirror Reaction

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Seed-mediated synthesis of silver nanocrystals with controlled sizes and shapes in droplet microreactors separated by air.

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

Influence of an Adsorption Layer and Its Evolvement on the Formation of Ag.

Influence of copper species on silver grain size in Ag–CuO–SiO2 ternary nanocomposites

Influence of adsorption of reactants on preparation of silver nanoparticles by adsorption phase synthesis

Studies on Preparation of Ag/SiO2 Nanocomposite and Its Electrical Properties

Morphology and Composition Controlled Synthesis of Flower-Like Silver Nanostructures.

Temperature Etching and Metallic Agent Concentration Effect on Structure, Morphology and Wettability of Silicon Nanowires

Toward Monodispersed Silver Nanoparticles with Unusual Thermal Stability.

Temperature Dependence of the Aggregation Mechanism of Silver Atoms Deposited on Liquid Substrates

Effects of Silver Nanoparticles on the Firing Behavior of Silver Paste on Crystalline Silicon Solar Cells

Preparation and Characterization of Ag Nanoshell on SiO2 Spheres via Electroless Plating Technique in Acidic Conditions

Preparation and Characterization of Ag Nanoshell on SiO/sub 2/ Spheres via Electroless Plating Technique in Acidic Conditions

Ag Nanoparticles Hosted in Monolithic Mesoporous Silica by Thermal Decomposition Method

Influence of Reaction Conditions on the Size and Distribution of Colloidal Silver Nanoparticles

Silver mirror reaction as a simple method for silicon nanowires functionalization

Epitaxial growth of silver nanoislands on the surface of silicon nanowires in ambient air

Role of Temperature in the Growth of Silver Nanoparticles Through a Synergetic Reduction Approach

Shape evolution and thermal stability of Ag nanoparticles on spherical SiO2 substrates