Abstract:Two kinds of adsorbates—L-ascorbic acid and NaOH were used separately to investigate the effects of adsorbate distribution between ethanol bulk phase and the phase of water-rich layer adsorbed by the surface of SiO2 particles on the preparation of silver nanoparticles on SiO2 particles. When the adsorbate L-ascorbic acid was used, L-ascorbic distributes mainly in the ethanol bulk phase and thus the Ag particle generating reaction will take place in the ethanol bulk phase with the generated Ag particle size of about 18 nm. When the adsorbate NaOH was used, NaOH distributes mainly in the phase of water-rich layer adsorbed on the surface of SiO2 particles and thus the Ag particles generate in the water-rich adsorption layer with particle size of only about 5.4 nm. Since the NaOH concentration effects its distribution between the two phases of ethanol bulk phase and water-rich adsorption layer, the further experiments with changing NaOH concentration in the reaction system from 0.0170 to 0.404 g·L-1 were conducted. Results show that when concentration of NaOH in the system was increased from 0.0170 to 0.135 g·L-1, the NaOH concentration in the water-rich adsorption layer increases with the increase of NaOH concentration in the system gradually, which causes the generation of Ag grains gradually centralizes in the adsorption layer with the grain size decreases from 8 nm to 5 nm, and the Ag particles generated cover the SiO2 more uniformly. When NaOH concentration in the system was increased from 0.135 to 0.404 g·L-1, the amount of NaOH in the system is over the maximum NaOH capacity that can be contained in the water-rich adsorption layer and thus the NaOH concentration in ethanol bulk phase will increase to the limit, above which, the Ag generating reaction rate in it will accelerate more quickly than that in the water-rich adsorption layer, which causes the main generation zone of silver nanoparticles moves from water-rich adsorption layer to ethanol bulk phase gradually, and at the same time, the generated Ag grain size will increase from 5 nm to 12 nm.

Influence of Reaction Conditions on the Size and Distribution of Colloidal Silver Nanoparticles

Influence of adsorption of reactants on preparation of silver nanoparticles by adsorption phase synthesis

Effect of Interphase Distribution of Reactants in Binary Liquids on Preparation of Silver Nanoparticles on Silica Particles

Influence of copper species on silver grain size in Ag–CuO–SiO2 ternary nanocomposites

Preparation and Characterization of Stable Dispersive Colloidal Silver Nanoparticles

Effect of Polyvinyl Pyrrolidone Molecular Weights on the Formation of Nanosized Silver Colloids

Synthesis of nanosized silver particles by chemical reduction method

Preparation and Microstructure of Silver Nanopowder with Spheric Morphology

Studies on the Continuous Precipitation of Silver Nanoparticles

Size Controllable Synthesis of Ultrafine Silver Particles Through a One-Step Reaction

Synthesis of Silver Nanocubes and Factors Affecting the Size and Shape of Sliver Nanoporticles

Effects of PVP on properties of micro-sized silver powders prepared by liquid phase reduction method

Effect of Storage Conditions on the Stability of Colloidal Silver Solutions Prepared by Biological and Chemical Methods

Preparation of Ultrafine Silver Powder by Reduction of Glucose

Particle size control and the interactions between drug and stabilizers in an amorphous nanosuspension system

Preparation and Characterization of Silver Powders with Spheric Shape and Different Sizes

The Effect of pH on the Size of Silver Nanoparticles Obtained in the Reduction Reaction with Citric and Malic Acids

Preparation of Silver Nanoparticles Colloid by Pulsed Laser Ablation

Synthesis of Silver and Gold Nanoparticles by a Novel Electrochemical Method

The effect of reaction factors on the morphology of silver particles prepared by chemical reduction method

Nanocrystalline Silver Particles: Synthesis, Agglomeration, and Sputtering Induced by Electron Beam.