Effect of Zr substitution on the structure and magnetic properties of (Y, Zr)(Fe, Ti) 12 compounds
Shaohua Fan,Fanggui Wang,Yuanhua Xia,Baochun Wu,Hui-Dong Qian,Zhongchong Lin,Yuankang Wang,Honglin Du,Jinbo Yang,Yingchang Yang
DOI: https://doi.org/10.1016/j.mtphys.2023.101119
IF: 11.021
2023-05-23
Materials Today Physics
Abstract:Fe-rich ThMn 12 -type intermetallic compounds have attracted wide attention due to high potential in advanced permanent magnet motors. However, the necessary addition of the third elements M to stabilize the ThMn 12 -type structure leads to a substantial decrease of M s , which becomes a barrier to improve the intrinsic magnetic properties. Some studies showed that substituting Zr for R at the 2 a site helped reduce the content of M. In this paper, the effect of Zr substitution on the structure and magnetic properties of (Y, Zr)(Fe, Ti) 12 compounds has been investigated utilizing neutron diffraction, magnetic measurement, and first-principles calculation. The results show that Zr substitution obviously enhances the stability and significantly reduces the content of Ti. In Y 1-x Zr x Fe 11.5 Ti 0.5 compounds, the competition between the magnetic volume effect and the chemical bonding effect of Zr leads to a maximum of M s when Zr = 0.2. In addition, Y 0.7 Zr 0.3 (Fe 0.75 Co 0.25 ) 11.7 Ti 0.3 compound containing the lowest content of Ti is successfully prepared, with M s and T c reaching 163.4 Am 2 /kg (12.26 kG) and 843.4 K, respectively. The highest M s of 167.7 Am 2 /kg (12.53 kG) and T c of 829.6 K are obtained in Y 0.7 Zr 0.3 (Fe 0.75 Co 0.25 ) 11.6 Ti 0.4 , which are superior to those of Nd-Fe-B and show great potential for permanent magnet applications.
materials science, multidisciplinary,physics, applied