Enhanced Magnetic Properties Of Disordered Rhombohedral 2 : 17 Type Alloys

Wb Yelon,Jb Yang,K Kamaraju,Wj James,Q Cai,Z Chu

2002-01-01

Abstract:A new disordered variant of the R2Fe17 structure (where R is a mixture of rare-earths) was recently described. It is found that more than 1/3 of the R atoms from the parent RT5 phase are replaced by Fe dumbbells, leading to a Fe-rich final composition. The Curie temperature is observed to increase with the dumbbell concentration and exceeds 600K in the best case. The formation of this variant appears to be controlled by the c/a ratio, which was originally adjusted with Si substitution for Fe and by the mixture of light and heavy rare earths. Reexamination of historic data on Y2Fe17+x shows that this structure may also be induced without Si substitution. Thus, this system (with a mixture of light rare earth and Y) shows promise for still higher Curie temperatures and remanence, since the net Fe content can be maximized. A series of alloys have been prepared by induction melting and characterized by neutron diffraction and magnetic measurements. These materials appear to be promising for practical magnet applications. Results on the (Nd0.5Dy0.5)(2-x)Fe17-ySiy and (Nd1-xYx)(2-z)Fe17-ySiy will be presented.