Abstract:The SO2/NOX pollution in the flue gas of non-ferrous smelting is increasingly serious. At the same time, the accumulation of red mud (RM) in the aluminum industry and phosphorus sludge (PS) in the yellow phosphorus industry has caused serious harm to the environment. To remove SO2 and NOX from the non-ferrous smelting flue gas and realize the resource utilization of the above two solid wastes, an ultrasonic field was used in this study to strengthen the PS excited O3 process and RM wet desulfurization and denitrification process. In the process of O3 excitation, the response surface method (RSM) is used to obtain the optimal O3 excitation concentration, and the optimal reaction conditions are designed based on the response surface optimization model: T is 53.226 °C, power density is 0.4 W/cm2, PS concentration is 51.433 g/L, O3 formation concentration up to 250 ppm or more, which provides a theoretical basis for subsequent desulfurization and denitrification steps. It is proved that this study can replace the expensive traditional O3 generator and provide a basis for NOX removal in the following process. In addition, the optimum experimental conditions of ultrasonic enhanced RM desulfurization and denitrification process were also explored. Under ultrasonic frequency of 28 kHz, ultrasonic power density of 0.4 W/cm2, T of 50 °C, RM concentration of 15 g/L, and stirring intensity of 1000 rpm, the desulfurization efficiency of the reaction system can be maintained above 95 % within 250 min, and the denitrification efficiency can be maintained above 90 % within 250 min. The effect of desulfurization and denitrification in this study is much better than that of traditional methods. Finally, the reaction mechanism of ultrasonic enhanced O3 excitation and RM wet desulfurization and nitrogen removal was discussed by combining adsorption thermodynamics, isotherm, and kinetics. The results showed that the OH· free radicals generated by ultrasonic cavitation and the physical effects brought by emulsification had significant promoting effects.

Study on the role of copper converter slag in simultaneously removing SO2 and NO using KMnO4/copper converter slag slurry

Mechanistic Study on the Enhanced SO2-tolerant Ability of CuCl2-promoted MnOx-CeOx Mixed Oxide for Hg0 Removal

Thermal modification of copper slag via phase transformation for simultaneous removal of SO2 and NOx from acid-making tail gas

[Inhibition of Sulfite Oxidation Catalyzed by Heavy Metals in Dual Alkali Flue Gas Desulfurization Slurry].

Efficient Removal of Sulfur Dioxide from Flue Gas Through Liquid Catalytic Oxidation Using Copper Tailing As the in Situ Iron Ion Donator

Simultaneous Removal of SO2 and NO by FeII(EDTA) Solution: Promotion of Mn Powder and Mechanism of Reduction

Removal of SO2 from Smelting Flue Gas by Using Copper Tailings with MnSO4: Factors Optimization by Response Surface Methodology

Treating waste with waste: Facile KHCO 3 -modified calcium carbide slag for simultaneous removal of NO and SO 2

Simultaneous Removal of SO2 and NO x Using Steel Slag Slurry Combined with Ozone Oxidation

An improved Wellman-Lord process for simultaneously recovering SO2 and removing NOX from non-ferrous metal smelting flue gas

Simultaneous Absorption of SO2 and NO from Flue Gas with KMnO4/CaCO3 Slurry

Ultrasonic-enhanced Phosphorus Sludge Excited O3 Coupled Red Mud Simultaneous Desulfurization and Denitrification

MgAlFeCu Mixed Oxides for SO2 Removal Capacity: Influence of the Copper and Aluminum Incorporation Method

Pretreated water-quenched-manganese-slag slurry for high-efficiency one-step desulfurization and denitrification

A Novel Double Metal Ions-Double Oxidants Coactivation System for NO and SO2 Simultaneous Removal

Oxidation and absorption of SO2 and NOx by MgO/Na2S2O8 solution at the presence of Cl−

Lab- and pilot-scale wet scrubber study on the redox-mediated simultaneous removal of NO and SO2 using a CaCO3-based slurry with KI as a redox catalyst

Simultaneous removal of SO2 and NO by using calcium absorbent with KMnO4 as additive

Ammoniacal System Mechanisms for Leaching Copper from Converter Slag

Effect of Additive Agents on the Simultaneous Absorption of No2 and So2 in the Calcium Sulfite Slurry

Studies on Simultaneous Catalytic Removal of NOX and SO2