High‐frequency and intrinsic dielectric properties of β‐CaSiO3 and its application: the microstrip patch antenna
Hongcheng Yang,Qian Liu,Zhan Wang,Yuandan Dong,Enzhu Li
DOI: https://doi.org/10.1111/jace.19619
IF: 4.186
2023-12-18
Journal of the American Ceramic Society
Abstract:β‐CaSiO3 LTCC material exhibit excellent stability of dielectric constant and loss at high frequencies (38;‐58 GHz and 70;‐90 GHz). A circularly polarized antenna using β‐CaSiO3 LTCC material was simulated and fabricated, which shows superior radiation efficiency (92.04 %) and gain (3.35 dBi) at the center frequency (2.5 GHz). Designing and fabricating antennas that exhibit low losses and are compact, lightweight, and highly radiation efficient are challenging in the wireless‐communication field. In this study, we simulated and fabricated microstrip patch antennas using β‐CaSiO3 low‐temperature co‐fired ceramic (LTCC) as dielectric resonator substrate. Compact ceramics that show good microwave dielectric properties (a relative dielectric constant [εr] of 6.57, high‐quality factor [Q × f] of 35 086 GHz [@14.85 GHz], and temperature coefficient of frequency [τf] of −33.56 ppm °C−1 for the optimal composition) were obtained when Li2O–CaO–B2O3–CuO glass was added to β‐CaSiO3 and sintered at 950°C. The high‐frequency properties of these composite ceramics reveal that the dielectric constant and dielectric loss are stable in the 38−58 and 70−90 GHz ranges, respectively. Furthermore, a circularly polarized antenna fabricated using a CaSiO3‐based ceramic shows a high radiation efficiency (92.04%) and gain (3.35 dBi) at a center frequency of 2.5 GHz. These β‐CaSiO3 composite ceramics offer promising prospects for high‐frequency use as well as in mobile communication applications. This study provides insight for the development of innovative antennas with new LTCC materials.
materials science, ceramics