Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Aqueous Synthesis of Highly Luminescent CdSe Quantum Dots with Narrow Spectra Using Hydrazine Hydrate Reduction Selenium

Simple Synthesis of Luminescent CdSe Quantum Dots from Ascorbic Acid and Selenium Dioxide.

Synthesis of high-quality CdSe quantum dots in aqueous solution

Aqueous Synthesis of Luminescent CdSe Quantum Dots from Selenium Tetrachloride

Preparation and Characterization of High Quality CdSe Quantum Dots in Aqueous Solution

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Aqueous Synthesis of Highly Luminescent Amorphous Cdse Quantum Dots at Low Temperature

Synthesis of Highly Emissive CdSe Quantum Dots by Aqueous Precipitation Method

Photo-assisted synthesis of highly fluorescent ZnSe(S) quantum dots in aqueous solution

Simple Synthesis of Highly Luminescent Water-Soluble CdTe Quantum Dots with Controllable Surface Functionality

Facile Synthesis and Characterization of Highly Luminescent Uv-Blue-Emitting Znse/Zns Quantum Dots Via A One-Step Hydrothermal Method

Aqueous synthesis of CdSe and CdSe/CdS quantum dots with controllable introduction of Se and S sources

One-Pot Synthesis of CdSe Quantum Dots Using Selenium Dioxide As a Selenium Source in Aqueous Solution

Highly Luminescent and Photostable Core/Shell/Shell ZnSeS/Cu:ZnS/ZnS Quantum Dots Prepared via a Mild Aqueous Route

Facile Synthesis and Optimization of ZnSe–GSH Quantum Dots by Hydrothermal Method

Aqueous synthesis of Cu-doped ZnSe quantum dots

Synthesis and Optical Properties of Water-Soluble CdTe1−Se Quantum Dots with Ultra-Long Fluorescence Lifetime

Significant Improvement in Photoluminescence of ZnSe(S) Alloyed Quantum Dots Prepared in High Ph Solution

Preparation of stable, water-soluble, highly luminescence quantum dots with small hydrodynamic sizes

Preparation and Luminescent Properties of CdSe and Core-Shell CdSe/CdS Quantum Dots in Aqueous Solution

Preparation of CdSe/CdS/SiO2 nanospheres and their luminescent properties