Abstract:The influence of Mo (10‐40at.%) additions to Cr‐8at.%Si was systematically studied by producing arc melted alloys and analyzing the as‐cast and annealed microstructures as well as the oxidation resistances. The majority of the alloys contained a solid solution A2 matrix with the intermetallic A15 = (Cr,Mo)3Si phase. The oxidation resistance was tested by thermogravimetric analysis (TGA) at 1200 °C in air for 50 and 100 h. Samples were characterized by XRD, SEM and EPMA (WDS). The studied Cr‐xMo‐8Si alloy series showed a beneficial effect of Mo on the corrosion behavior of the annealed arc melted alloys exposed at 1200 °C in air. An increased amount of A15 led to the formation of a continuous SiO2 scale beneath the Cr2O3 layer during high temperature exposure. The internal SiO2 layer inhibited further internal oxidation of the A15 phase. Prior annealing also influenced the oxidation behavior of the alloys. Higher annealing temperatures, resulted in an overall reduced fraction of the A15 phase, as well as coarsening, but also showed a more uniform size and distribution of the precipitates, which seems to benefit the formation of a protective duplex oxide scale. Cr‐25Mo‐8at.%Si annealed at 1350 °C for 100 h, showed the most promising oxidation behavior after exposure in air at 1200 °C for 100 h. For all of the investigated Mo contents, no nitridation was observed when compared to the Cr‐8Si reference composition. The oxide scale adhesion also was improved. For Mo >25 at.% no spallation was observed. Evaluation of the TGA data showed it follows the paralinear law, with both the growth rate, kp, and volatilization rate, kv, of Cr2O3 being reduced by adding 10‐25 at.% Mo. A binary Cr/Mo‐Si phase diagram was generated for the studied alloy series in order to determine accurate annealing conditions and estimate the stability range of the metastable σ phase. This article is protected by copyright. All rights reserved.

Effects of phase selection and microsegregation on corrosion behaviors of Ti-Al-Mo alloys

Effect of Mo Content on Microstructure and Properties of 00cr12ni9mo (x) Cu2Ti Maraging Stainless Steel

Effect of phase composition on the corrosion behavior of Ti-xMo alloy films

Effect of molybdenum content on corrosion resistance and corrosion behavior of Ti-Mo titanium alloy in hydrochloric acid

Effect of Mo Addition on Corrosion Behavior of High-Entropy Alloys CoCrFeNiMox in Aqueous Environments

The Effect of Molybdenum on the Corrosion Behaviour of the High-Entropy Alloys Co1.5crfeni1.5ti0.5mox in Aqueous Environments

Corrosion behaviors related to the microstructural evolutions of as-cast Al0.3CoCrFeNi high entropy alloy with addition of Si and Ti elements

Investigation on corrosion behavior of Zr-bearing TA10-based titanium alloys

Microstructure and Mechanical Properties and Corrosion Behavior of Ti-Mo-Sn Alloys

Corrosion resistance investigation of the Ti–Al–Mo system supported by CALPHAD approach and key experiments

Effect of Mo on Intergranular Corrosion Behavior in Super-austenitic Stainless Steel

Effects of alloying concentration on the aqueous corrosion and passivation of aluminum-manganese-molybdenum concentrated alloys

Effect of 2–6 At.% Mo Addition on Microstructural Evolution of Ti-44Al Alloy

Microstructure, mechanical properties and tribocorrosion characteristics of (Mo1-xCrx)5Si3 alloys

Effect of alloying elements (Mn, Ti, and Mo) on the corrosion behavior of FeCoNiCr-based high entropy alloy in supercritical water

THE INFLUENCE OF Mo‐CONTENT AND ANNEALING ON THE OXIDATION BEHAVIOUR OF ARC‐MELTED Cr‐xMo‐8Si ALLOYS

Effect of Molybdenum on the Pitting Resistance of Co1.5CrFeNi1.5Ti0.5Mox Alloys in Chloride Solutions

Effects of Al and Ti co-doping on the strength-ductility- corrosion resistance of CoCrFeNi-AlTi high-entropy alloys

Corrosion resistance of MoS2-modified titanium alloy micro-arc oxidation coating

Influence of α-Phase Morphology on Mechanical Characteristics, Cycle Oxidation, and Hot Corrosion Behavior of Ti-6Al-3Mo-2Nb-2Zr-2Sn-1.5Cr Alloy

Effect of electrochemical hydrogen charging on the mechanical property and corrosion behavior of Ti-3Mo alloy