Abstract:Ferroelectric LiNbO3 single crystals have piezoelectric, pyroelectric and electro-optic properties and are widely used in nonvolatile memories, sensors, and electro-optic modulators. The material is hard and relatively inert for dying etching using thick Cr/Ni mask layers which are incompatible with the CMOS manufacturing technologies. Moreover, the etching angles are generally below 80 degrees that could result in poor polarization retention and a large imprint effect. Here we developed an etching technique on the basis of the solid-state reaction and wet solution corrosion together that used CMOS-compatible SiO2 masks to fabricate large arrays of LiNbO3 nanodevices in high precision. The LiNbO3 nanopatterns at the regions beyond the SiO2 masks can react with the deposited Al metal below 500 degrees C in formation of amorphous layers in targeted thicknesses that vary with the annealing temperature and time at a reduced atmosphere. The amorphous layers can be dissolved in mixed solutions of H2O, NH4OH, and H2O2 at 85 degrees C, and the etching angles of memory cells in lateral sizes of 20-220 nm can approach 90 degrees after the passivation of the LiNbO3 surface layer. The transmission electron microscope study shows the oxygen deficiency at the surface. After the connection of the cell to two side electrodes, domain switching occurs under an applied horizontal electrode field along the polar Z-axis accompanying the formation of conducting domain walls against the peripheral unswitched domain at the substrate. The read current can highly reach the level of 2-20 mu A in high reliability. This etching technique promotes the large-scale fabrication of LiNbO3 nanodevices on the Si platform.

Hard Mask Free Drie Of Crystalline Si Nanobarrel With 6.7nm Wall Thickness And 50:1 Aspect Ratio

Fabrication of ultrahigh-aspect-ratio and periodic silicon nanopillar arrays using dislocation lithography and deep reactive-ion etching

Reduction in Modulus of Suspended Sub-2 nm Single Crystalline Silicon Nanomembranes

Optimization of Photoresist Development and DRIE Processes to Fabricate High Aspect Ratio Si Structure in 5nm Scale

Post-CMOS Processing for High-Aspect-Ratio

Nanofabrication of high aspect ratio structures using an evaporated resist containing metal

High aspect ratio nano-fabrication of photonic crystal structures on glass wafers using chrome as hard mask

Development of a facile block copolymer method for creating hard mask patterns integrated into semiconductor manufacturing

High Aspect Ratio Etching of Nanopores in PECVD SiC Through AAO Mask

A route to engineered high aspect-ratio silicon nanostructures through regenerative secondary mask lithography

High aspect ratio arrays of Si nano-pillars using displacement Talbot lithography and gas-MacEtch

Fabricating 3D Si nanostructure via a novel Ga+ implantation enabled maskless dry etching process

Wafer-Scale Fabrication of Ultra-High Aspect Ratio, Microscale Silicon Structures with Smooth Sidewalls Using Metal Assisted Chemical Etching

A single-mask dry-release process for fabrication of high aspect ratio SOI MEMS devices

Low-temperature plasma etching of high aspect-ratio densely packed 15 to sub-10 nm silicon features derived from PS-PDMS block copolymer patterns

Fabrication of ultra-high-aspect-ratio nano-walls and nano-structures on silicon substrates

A Single Mask Dry Releasing Process for Making High Aspect Ratio Soimemsdevices.

Post-CMOS Process for High-Aspect-ratio Monolithically Integrated Single Crystal Silicon Microstructures

Nanometer-sized Etching of Lithium Niobate Domain Wall Devices

3‐D Nanofabrication of Silicon and Nanostructure Fine‐Tuning via Helium Ion Implantation

Wafer Scale Fabrication of Dense and High Aspect Ratio Sub-50 Nm Nanopillars from Phase Separation of Cross-Linkable Polysiloxane/Polystyrene Blend