Contrasting Thermoelectric Properties in cubic SnSe-NaSbSe 2 and SnSe-NaSbTe 2 : High Performance Achieved via Increasing Cation Vacancies and Charge Densities

Yuping Wang,Bingchao Qin,Haonan Shi,Lizhong Su,Dongyang Wang,Li-Dong Zhao

DOI: https://doi.org/10.1016/j.actamat.2023.118754

IF: 9.4

2023-02-08

Acta Materialia

Abstract:Cubic SnSe has been recognized as one of the most promising mid-temperature thermoelectric candidates. Herein, the cubic-phase SnSe has been stabilized at room temperature by alloying NaSbSe 2 and NaSbTe 2 , respectively, and the contrasting thermoelectric properties of SnSe-NaSbSe 2 and SnSe-NaSbTe 2 were systematically investigated. NaSbTe 2 -alloyed SnSe demonstrates better performance with especially higher electrical properties. According to the DFT calculations, the introduction of NaSbTe 2 can bring the lattice parameter of cubic-phase SnSe closer to SnTe, leading to a lower cation vacancy formation energy and producing an ultra-high hole carrier concentration. Meanwhile, Te has a more developed charge density compared with that of Se, providing additional channels for charge transport when bonded to Sn atoms in cubic lattice. Limited by the electrical transport properties, the ZT max for SnSe-NaSbSe 2 only reaches ∼ 0.50 at 773 K, while the ZT max for SnSe-NaSbTe 2 approaches ∼ 0.95. Furthermore, sodium doping was utilized to tune the carrier mobility and carrier concentration of SnSe-NaSbTe 2 . Resultantly, the PF max and ZT max values reach ∼ 11 μW cm −1 K −2 and ∼ 1.20 at 773 K in sodium-doped SnSe-NaSbTe 2 , 4.4 and 3.0 times higher than those of pure SnSe, respectively. Our study further promotes cubic-phase SnSe thermoelectrics for mid-temperature energy harvesting applications.

materials science, multidisciplinary,metallurgy & metallurgical engineering