Abstract:Microcracks are easily generated inside polymers and polymer composites during their service in structural applications. Development and coalescence of microcracks would bring about catastrophic failure of the materials and then reduce their lifetimes. Therefore, early sensing, diagnosis and repair of microcracks become necessary for removing the latent perils. In this context, the materials possessing self-healing function are ideal for long-term operation. Attempts have been made to develop solutions in this filed, among which the route based on microcapsulation seems to be promising. Self-repairing polymer composites containing microencapsulated healing agent have attracted more and more research interests. The present article analyzed the existing problems and proposed the criteria for manufacturing qualified microencapsulated healing agent. Accordingly, microcapsules containing epoxy resin were successfully fabricated by in situ polymerization in an oil-in-water emulsion with poly(melamine-formaldehyde) (PMF) as the shell material and high-activity low-viscosity diglycidyl tetrahydro-o-phthalate (DTP) as the core substance. The typical synthesis procedures are described below. About 50 g DTP was added into 250 mL aqueous solution of 2 % styrene-maleic sodium (SMS). The mixture was vigorously agitated by a homogenizer for 10 min at a selected rate and then two drops of I-octanol were added to eliminate surface bubbles of the emulsion. The pre-condensate of 12.5 g melamine and 27.1 g formaldehyde was prepared at 70 similar to 75 degrees C for 30 min, and the pH value of the solution was kept at about 9 similar to 10 by adding triethanolamine. Subsequently, the precondensate solution was added to the above emulsion with 450 r/min continuous mechanical stirring by a two-bladed stirring paddle while the pH value of the solution was adjusted by adding citric acid. Eventually, the reaction mixture was cooled down to room temperature. The resultant slurry was neutralized by 2 % sodium carbonate solution, and then diluted with deionized water. The deposit of microcapsules was separated through a Buchner funnel and rinsed with deionized water and then vacuum dried. The synthesis method was improved by optimizing the processing parameters. The appropriate reaction time was about 30 similar to 60 min. Further extension of time had little influence on the products. The reaction temperature should be set at about 50 similar to 70 degrees C. The pH value of about 3.2 was appropriate and had complex effect on the properties of the products. The appropriate core/shell mass ratio was about 2:1 similar to 3:1. The size and size distribution of microcapsules were mainly determined by the dispersion rate and the emulsifier content. Having been encapsulated, the core material DTP kept the same activity as its raw version. The microcapsules' shell wall was relatively thin (ca. 0. 2 mu m), which assured sufficient core content (83.2 wt %) even if the microcapsules were very small (ca. 6.7 mu m). Moreover, the microcapsules were proved to be strong enough to survive handling during manufacturing self-healing composites. Having been pre-embedded in cured epoxy, the microcapsules had satisfied affinity to the matrix. They can be readily ruptured releasing DTP fluid as expected upon damaging of the composite, and activity of the released core material was the same as the raw material. Besides, the microcapsules had good sealing ability and high stability. They can be stored at room temperature for long time and could bear moderate or high temperatures applied for curing composites.The resent work provided a new simple approach for mass-production of epoxy loaded microcapsules, which can be used to manufacture self-healing composites or other self-curing stuffs like single constituent epoxy adhesive and self-locking threaded fasteners.

Preparation and Characterization of Self-healing Polymeric Materials with Microencapsulated Epoxy and Imidazoline Derivatives Curing Agent

Preparation and Properties of Self-healing Coatings Containing Epoxy Resin Microcapsules

Study On Preparation and Mechanism of Self-healing Poly(urea-formaldehyde) Microcapsules

Study on the curing kinetics of epoxy resin in self-healing microcapsules with different shell material

Preparation And Application Of Melamine-Urea-Formaldehyde Self-Healing Microcapsules Modified By Nano-Al2o3

Self-healing Epoxy Composites – Preparation and Effect of the Healant Consisting of Microencapsulated Epoxy and Latent Curing Agent

Self-healing Epoxy Based on Cationic Chain Polymerization

Self-Healing Polymeric Materials Using Epoxy/Mercaptan As The Healant

A Novel Self-Healing Epoxy System with Microencapsulated Epoxy and Imidazole Curing Agent

Preparation and Characterization of Poly (Melamine-Formaldehyde) Walled Microcapsules Containing Epoxy

Study of Factors Related to Performance Improvement of Self-Healing Epoxy Based on Dual Encapsulated Healant

Preparation and Characterization of Microencapsulated Ethylenediamine with Epoxy Resin for Self-healing Composites

Microencapsulation of Ethylenediamine and Its Application in Binary Self-Healing System Using Dual-Microcapsule

High‐performance self‐healing epoxy by microencapsulated epoxy‐amine chemistry II: Performance of the system

Investigation on Microcapsule Self‐healing Mechanism of Polymer Matrix Composites Based on Numerical Simulation

Self-Healing of Cracks in Epoxy Composites

Preparation and Self-Healing Application of Isocyanate Prepolymer Microcapsules

Free Radical Polymerization Aided Self-Healing

Self Healing System for Concrete Surface Crack using Polymer based Coating Agent Incorporating Microencapsulated Healing Agent

The Preparation and Research of Microcapsules in Self-Healing Coatings

Styrene and BPO Poly (Urea-Melamine-formaldehyde) Microcapsules Prepared Via in Situ Polymerization to Promote the Self-Healing Properties of Epoxy Composites