Self-healing Epoxy Based on Cationic Chain Polymerization

Ding Shu Xiao,Yan Chao Yuan,Min Zhi Rong,Ming Qiu Zhang
DOI: https://doi.org/10.1016/j.polymer.2009.04.029
IF: 4.6
2009-01-01
Polymer
Abstract:A two-component healing agent consisting of epoxy- and ((C2H5)2O·BF3)-loaded microcapsules was synthesized and applied to fabricate self-healing epoxy composites. Curing of epoxy healing agent catalyzed by (C2H5)2O·BF3 belongs to cationic chain polymerization, which is characterized by fast reaction at ambient temperature and low catalyst concentration. The experimental results showed that cracks in the composites containing the above healing system can be quickly re-bonded with satisfied healing efficiency. In the case of 5wt% epoxy- and 1wt% (C2H5)2O·BF3-loaded capsules, for example, a ∼80% recovery of impact strength was detected within 30min at 20°C. Because the healing capsules took effect at low content, mechanical properties of the matrix were largely retained. It is believed that the present healing system provides a possible solution to preparation of self-healing polymeric materials with practical applicability.
What problem does this paper attempt to address?